User:Stephanie Tietz/Notebook/Stephanies Notebook/2013/05/13: Difference between revisions
From OpenWetWare
(→Gel) |
(fix raw html notebook nav) |
||
(3 intermediate revisions by one other user not shown) | |||
Line 2: | Line 2: | ||
|- | |- | ||
|style="background-color: #EEE"|[[Image:owwnotebook_icon.png|128px]]<span style="font-size:22px;"> Project name</span> | |style="background-color: #EEE"|[[Image:owwnotebook_icon.png|128px]]<span style="font-size:22px;"> Project name</span> | ||
|style="background-color: #F2F2F2" align="center"| | |style="background-color: #F2F2F2" align="center"|[[File:Report.png|frameless|link={{#sub:{{FULLPAGENAME}}|0|-11}}]][[{{#sub:{{FULLPAGENAME}}|0|-11}}|Main project page]]<br />{{#if:{{#lnpreventry:{{FULLPAGENAME}}}}|[[File:Resultset_previous.png|frameless|link={{#lnpreventry:{{FULLPAGENAME}}}}]][[{{#lnpreventry:{{FULLPAGENAME}}}}{{!}}Previous entry]] }}{{#if:{{#lnnextentry:{{FULLPAGENAME}}}}|[[{{#lnnextentry:{{FULLPAGENAME}}}}{{!}}Next entry]][[File:Resultset_next.png|frameless|link={{#lnnextentry:{{FULLPAGENAME}}}}]]}} | ||
|- | |- | ||
| colspan="2"| | | colspan="2"| | ||
Line 25: | Line 25: | ||
***BSA solution = 10.57mL | ***BSA solution = 10.57mL | ||
*1mL was siphoned from each solution and added to 8mL of purified water. | *1mL was siphoned from each stock solution and added to 8mL of purified water. | ||
*The 10mL Au+BSA+H<sub>2</sub>O solution was then put into the oven for approximately 4 hours. | *The 10mL Au+BSA+H<sub>2</sub>O solution was then put into the oven for approximately 4 hours. | ||
Line 31: | Line 31: | ||
==Gel== | ==Gel== | ||
*10mL of water was added to 1.682 g poly(vinyl alcohol) (130,000 molecular weight) | *10mL of water was added to 1.682 g poly(vinyl alcohol) (130,000 molecular weight) | ||
**This solution was heated and stirred for approximately | **This solution was heated and stirred for approximately one hour at 80°C until a homogeneous gel remained | ||
*1mL of .25 mM Au and 1mL of 1.7857 μM BSA were added to the beaker with the poly(vinyl alcohol)+H<sub>2</sub>O solution | |||
**After stirring the new solution, it was placed in the oven | |||
Latest revision as of 22:42, 26 September 2017
Project name | Main project page Next entry |
Nanoparticle Fiber
Gel
|