Last time you proposed culture conditions for an investigation of chondrocyte phenotype induction or maintenance, and today you will initiate said cultures. The chondrocyte cells you are using were freshly derived from bovine cartilage by enzymatic digestion and immediately frozen. The stem cells were grown from bovine bone marrow over the course of a few weeks, then frozen after 1-2 passages. Cells from cows are often used in part because of their availability from abattoirs. In general, large animals are more useful for modeling human joint diseases such as osteoarthritis than are small animals, because the resting angle of their knee joints is more similar to that of humans. In this module, we will work with an in vitro culture model of cartilage-forming cells.
Your two cell samples will be grown in alginate bead cultures. You have probably encountered alginates many times in your life, as thickeners in food and textiles, preservatives, and possibily at your dentist or in a pharmacy. Alginate is a polysacharride derived from seaweed, a co-polymer of mannuronic and guluronic acid. A single alginate molecule may contain long stretches of either acid (called M-blocks and G-blocks), as well as random and/or strictly alternating G/M sequences. The precise chemical composition of an alginate determines its mechanical properties, degradability, and other important characteristics. Qualities such as strength and viscosity are also influenced by the average length of the individual polymer chains (i.e., the molecular weight), and by alginate concentration. For example, high molecular weights correlate with increased viscosity. Alginates in general are shear-thinning, which is to say their viscosity decreases as shear rate increases (e.g., when quickly drawn into a syringe).
Schematic of crosslinked-alginate.
G-blocks are represented by dotted lines, M-blocks by curved solid lines, and calcium ions by green circles.
Cations such as calcium can cross-link alginate chains to form a network, or gel. The identity and concentration of the cross-linker influence the ultimate material properties. Only G-blocks can be linked to each other, while M- or MG-blocks cannot, but in turn provide flexibility (see figure). The resultant semi-solid structure has the capacity to hold a large amount of water, and the water-swollen structure is called a hydrogel. Hydrogels have several attractive properties for tissue engineering: they allow oxygen and nutrients to diffuse better than non-hydrated materials do; their mechanical and biochemical properties are readily varied by co-polymerization of multiple elements; they mimic the elasticity of natural tissues, and they often form rapidly and under mild conditions. Some gels can be injected into a patient in liquid form, then solidified within his or her body by heat or light. Such injectable gels have the advantage of easily filling an arbitrarily sized wound shape, which is difficult for implantable gels to do. Natural (e.g., alginate) and synthetic (e.g., poly(ethylene glycol)) hydrogels each have distinct advantages and disadvantages, as we will discuss in class.
Today you will make alginate hydrogels in bead form, by slowly releasing alginate solution from a syringe into a bath containing calcium chloride. Next time you will see how well your cells survived.
Half the class at a time will work in the tissue culture room today. Today will be physically and mentally laborious, and you've all been working hard, so spend the rest of the afternoon however you see fit. (Whether that involves the FNT assignment, notebook prep, or a walk in the sunshine - are we still expecting sunshine?)
Chondrocyte or stem cell culture
Today you will work with primary cells that are directly isolated from bovine knee joints. Recently, your teaching faculty harvested cartilage fragments from three bovine knees, and sequentially digested them in pronase and collagenase enzymes to release the chondrocytes. Each joint typically yields > 50-100M cells. Stem cells were harvested from the bone marrow and grown up from a rare population by extended culture in bFGF (basic fibroblast growth factor). After cell isolation, aliquots of several million cells each were frozen and stored in liquid nitrogen.
- Begin by setting up your hoods. Prepare any standard equipment and solutions needed.
- Note that the small beakers are for making a calcium chloride bath (not shared, one per person), and the large are for temporary waste in steps 10-12 below (shared, one per hood).
- If you requested a special reagent or equipment, check with the teaching faculty.
- If you are doing an alternative protocol (e.g., 2D culture or collagen gels), check with the teaching faculty.
- When your hood is ready, thaw your aliquot(s) of frozen cells in the water bath. Avoid immersing the cap of the tube in the bath; just hold the body submerged. Agitate the vial slightly while you hold it. The cells should thaw in less than 5 minutes.
- Spray the vial with 70% ethanol and take it into your hood. Using a P1000, add the cells drop-wise into the 15 mL conical containing 9 mL of pre-warmed medium. Spin at 800 g for 8 minutes.
- Aspirate most of the medium off your cell pellet, then gently resuspend in 1 mL of medium using your P1000. Add 3 mL more of medium per vial, using a serological pipet for the addition and subsequent mixing of the medium and cells. Take 90 μL of cells into an eppendorf tube.
- Add 10 μL of Trypan blue - this is a toxic material, so please be careful not to spill it! - to the eppendorf tube, and count your cells. Adjust your culture plan if you do not have as many cells as you expected.
- No need to count all 4 corners today - perhaps count 2, especially if your cell count is high.
- Separate the cells that will make up your two different cultures into two labeled 15 mL conical tubes. Note that the tubes may not all require the same amount of cells, depending on the cell densities you chose for the two cultures. Double-checking your calculations now may save you having to do an extra centrifugation step later!
- Give any excess cells that you have to the teaching faculty, in case other groups want more cells.
- Spin down your two conical tubes of cells at 800 g for 8 minutes.
- Resuspend each sample of cells in the appropriate amount of the type and concentration of alginate that you chose (1 mL per condition).
- Using the syringe that has been prepared for you, very carefully pull up the cells, and then release them drop-by-drop into the beaker full of calcium chloride solution (20 mL). Recall that calcium effectively polymerizes the alginate, resulting in small gel beads filled with cells. Immediately discard the entire syringe into the sharps jar in your hood - do not try to remove or recap the needle.
- Don't release too quickly or you will get a glob instead of distinct droplets, and try to match your release rate and height above the solution (not too high!) with your partner's.
- Depending on the concentration of alginate that you chose, you may have between ~50-150 beads for 1 mL of alginate solution.
- Allow the polymerization to proceed for 10 min. at room temperature. Then pour your beads into a 50mL conical tube.
- Remove the calcium chloride solution from your beads using a large serological pipet (to better avoid aspirating the beads), and put this solution in the temporary waste beaker in your hood.
- Ask the teaching faculty for tips on avoiding sucking up your beads. Basically, you want to keep the pipet close to the wall of the conical tube, so liquid can still be sucked up but the beads don't have room to be.
- Now fill the conical tube with sodium chloride (20 mL), and gently invert it for 1-2 min. This is to remove excess calcium from the solution.
- Remove the NaCl using a fresh pipet, and then wash the beads again with fresh NaCl. Finally, wash the beads two times with DMEM culture medium (20 mL each time).
- At this step, you will wash with DMEM that doesn't contain all of the additives needed for successful culture.
- For each of your two samples, transfer the beads to the two leftmost wells of a 6-well plate, using a sterile spatula. Try to put approximately equal numbers of beads in the two wells.
- Finally, add 6 mL of warm culture medium to each of your four sample wells, and then put the two well-plates in the incubator.
- Be sure to use the complete medium – different for chondrocytes and stem cells – at this step.
- Don't forget to add the appropriate additive(s) to (some of) your media, if you have requested additional ones.
The teaching faculty will exchange the culture medium as necessary (either a half medium exchange every day or a full medium exchange every other day).
For next time
- Sign up for a time to do your Day 3 lab work on the Day 3 Talk page; on this day you will arrive at staggered times.
- That's it!
- Media as described on Day 1, or with special additives if requested
- Alginates as described/requested on Day 1
- 102 mM CaCl2
- 0.15 M NaCl
- Trypan blue, 0.4%