User:Michael S. Bible/Notebook/Summer MOF Research/2016/07/22: Difference between revisions
From OpenWetWare
(Autocreate 2016/07/22 Entry for User:Michael_S._Bible/Notebook/Summer_MOF_Research) |
(fix raw html notebook nav) |
||
(One intermediate revision by one other user not shown) | |||
Line 2: | Line 2: | ||
|- | |- | ||
|style="background-color: #EEE"|[[Image:owwnotebook_icon.png|128px]]<span style="font-size:22px;"> Project name</span> | |style="background-color: #EEE"|[[Image:owwnotebook_icon.png|128px]]<span style="font-size:22px;"> Project name</span> | ||
|style="background-color: #F2F2F2" align="center"| | |style="background-color: #F2F2F2" align="center"|[[File:Report.png|frameless|link={{#sub:{{FULLPAGENAME}}|0|-11}}]][[{{#sub:{{FULLPAGENAME}}|0|-11}}|Main project page]]<br />{{#if:{{#lnpreventry:{{FULLPAGENAME}}}}|[[File:Resultset_previous.png|frameless|link={{#lnpreventry:{{FULLPAGENAME}}}}]][[{{#lnpreventry:{{FULLPAGENAME}}}}{{!}}Previous entry]] }}{{#if:{{#lnnextentry:{{FULLPAGENAME}}}}|[[{{#lnnextentry:{{FULLPAGENAME}}}}{{!}}Next entry]][[File:Resultset_next.png|frameless|link={{#lnnextentry:{{FULLPAGENAME}}}}]]}} | ||
|- | |- | ||
| colspan="2"| | | colspan="2"| | ||
<!-- ##### DO NOT edit above this line unless you know what you are doing. ##### --> | <!-- ##### DO NOT edit above this line unless you know what you are doing. ##### --> | ||
== | ==Create DSC Samples== | ||
* | * DSC samples were prepared from the 10% MOF-5, 10% HKUST-1, 10% ZIF-8, 50% MOF-5, and ABS filaments. | ||
* Each sample consists of the following masses: | |||
* '''10% MOF-5''': Sample Mass - 2.96 mg, DSC Pan mass - 39.99 mg | |||
* '''10% ZIF-8''': Sample Mass - 3.13 mg, DSC Pan mass - 40.09 mg | |||
* '''10% HKUST-1''': Sample Mass - 3.27 mg, DSC Pan mass - 40.02 mg | |||
* '''50% MOF-5''': Sample Mass - 2.89 mg, DSC Pan mass - 40.17 mg | |||
* '''ABS''': Sample Mass - 3.23 mg, DSC Pan mass - 39.01 mg | |||
==Create PXRD Samples== | |||
* PXRD samples were created from the 50% MOF-5 in ABS filament and 10% HKUST-1 in ABS filament. | |||
* About 1.05g of each was pressed at 195 °C | |||
* The discs were removed and still had very noticeable grain boundaries, so they were re-pressed at 220°C | |||
* Despite the increased temperature, the materials still did not appear homogeneous. It was determined, however, that this would be sufficient for PXRD. | |||
<!-- ##### DO NOT edit below this line unless you know what you are doing. ##### --> | <!-- ##### DO NOT edit below this line unless you know what you are doing. ##### --> |
Latest revision as of 01:50, 27 September 2017
Project name | Main project page Previous entry Next entry |
Create DSC Samples
Create PXRD Samples
|