User:Matthew R Skorski/Notebook/Cellulose Summer 2014/2014/09/10: Difference between revisions
(fix raw html notebook nav) |
|||
(3 intermediate revisions by one other user not shown) | |||
Line 2: | Line 2: | ||
|- | |- | ||
|style="background-color: #EEE"|[[Image:owwnotebook_icon.png|128px]]<span style="font-size:22px;"> Project name</span> | |style="background-color: #EEE"|[[Image:owwnotebook_icon.png|128px]]<span style="font-size:22px;"> Project name</span> | ||
|style="background-color: #F2F2F2" align="center"| | |style="background-color: #F2F2F2" align="center"|[[File:Report.png|frameless|link={{#sub:{{FULLPAGENAME}}|0|-11}}]][[{{#sub:{{FULLPAGENAME}}|0|-11}}|Main project page]]<br />{{#if:{{#lnpreventry:{{FULLPAGENAME}}}}|[[File:Resultset_previous.png|frameless|link={{#lnpreventry:{{FULLPAGENAME}}}}]][[{{#lnpreventry:{{FULLPAGENAME}}}}{{!}}Previous entry]] }}{{#if:{{#lnnextentry:{{FULLPAGENAME}}}}|[[{{#lnnextentry:{{FULLPAGENAME}}}}{{!}}Next entry]][[File:Resultset_next.png|frameless|link={{#lnnextentry:{{FULLPAGENAME}}}}]]}} | ||
|- | |- | ||
| colspan="2"| | | colspan="2"| | ||
Line 18: | Line 18: | ||
1.0% 0.2493 g 25.0014 g | 1.0% 0.2493 g 25.0014 g | ||
Added 250 mL acetone to TiO<sub>2</sub>. Sonicated from 9:25 am to 9:40 am at 23°C to 27°C. Added ABS and sonicated from 9:40 am at 23°C to 4:20 pm at 43°C. When the solution was put into the pan small ABS specks were noticed. Heated the pan at 80°C from 4:20 pm to | Added 250 mL acetone to TiO<sub>2</sub>. Sonicated from 9:25 am to 9:40 am at 23°C to 27°C. Added ABS and sonicated from 9:40 am at 23°C to 4:20 pm at 43°C. When the solution was put into the pan small ABS specks were noticed. Heated the pan at 80°C from 4:20 pm to 7:00 pm. | ||
This TiO<sub>2</sub> is white and not tan like the previous TiO<sub>2</sub> from the summer. TiO<sub>2</sub> from the summer was < 100 nm large and contained 1% Mn as dopant. TiO<sub>2</sub> for this fall is 21 nm large and does not have Mn as a dopant. | This TiO<sub>2</sub> is white and not tan like the previous TiO<sub>2</sub> from the summer. TiO<sub>2</sub> from the summer was < 100 nm large and contained 1% Mn as dopant. TiO<sub>2</sub> for this fall is 21 nm large and does not have Mn as a dopant. | ||
Line 24: | Line 24: | ||
Figure 1: TiO<sub>2</sub> powder | Figure 1: TiO<sub>2</sub> powder | ||
Figure 2: ABS specks left on glass after pouring into pan. | [[Image:20140910 092045.jpg]] | ||
Figure 2: ABS specks left on glass after pouring into pan. | |||
[[Image:20140910 162305.jpg]] | |||
Figure 3: Casting next morning | |||
[[Image:20140911 102230.jpg]] | |||
Latest revision as of 00:16, 27 September 2017
Project name | Main project page Previous entry Next entry |
Entry titlePurpose: Create 25 g cast of TiO2 1% Safety and Procedure: Normal large casting, see 6/18/14, but with 250 mL of acetone instead of 200. Experimental: Created a 25 g TiO2 cast Mass % Mass TiO2 Mass ABS 1.0% 0.2493 g 25.0014 g Added 250 mL acetone to TiO2. Sonicated from 9:25 am to 9:40 am at 23°C to 27°C. Added ABS and sonicated from 9:40 am at 23°C to 4:20 pm at 43°C. When the solution was put into the pan small ABS specks were noticed. Heated the pan at 80°C from 4:20 pm to 7:00 pm. This TiO2 is white and not tan like the previous TiO2 from the summer. TiO2 from the summer was < 100 nm large and contained 1% Mn as dopant. TiO2 for this fall is 21 nm large and does not have Mn as a dopant. Figure 1: TiO2 powder Figure 2: ABS specks left on glass after pouring into pan. Figure 3: Casting next morning
|