Objective
- Make 5 sets of PLA scaffolds: untreated PLA scaffolds, nanofiber-coated scaffolds by Brute-force method, biomineralization method of nanofiber formation with scaffolds, polydopamine-coated scaffolds, and polydopamine nanofiber-coated scaffolds
- Collect result data from last lab
Methods
- Each set consisted of 3 test tubes, each containing 4 stacked PLA scaffolds.
- All scaffolds were Autoclaved at then end of each procedure.
Plain scaffold
- The scaffolds were submerged in water
Brute Force method
- 100:1 Au:Myoglobin nanofibers were made based on previous biomineralization protocol
- The nanofibers were then place onto the scaffolds and allowed to dry
- The dry nanofiber-coated scaffolds were then submerged in water
Old method + scaffolds
- 100:1 Au:Myoglobin nanofibers were made following previously used protocol, but with the PLA scaffolds in the test tubes
Polydopamine-coated scaffolds
- Scaffolds submerged in 10mM pH 8.46 TRIS dopamine hydrochloride solution for 1 hour
- Add 1mL of 0.0621 Myoglobin to each test tube, shake tube to combine, allow surface functionalization to occur for 5 hours
- Rinse with deionized water and allow scaffold to dry overnight
- Scaffolds submerged in water
Polydopamine Nanofiber-coated scaffolds
- Scaffolds submerged in 10mM pH 8.46 TRIS dopamine hydrochloride solution for 1 hour
- Add 1mL of 0.0621 Myoglobin to each test tube, shake tube to combine, allow surface functionalization to occur for 5 hours
- Rinse with deionized water and allow scaffold to dry overnight
- Scaffolds submerged in water
- Gold:Myoglobin (100:1) nanofibers synthesized by above procedure with polydopamine-coated scaffolds in solution
Results
Ag:BSA Nanofibers: Results from 02/25/2014
- Set 1 (All ratios, room temperature)
<br.>
- Set 2 (All ratios, heated to 80C)
<br.>
- Set 3 (All ratios plus 1uL Au, heated to 80C)
<br.>
|