User:Moira M. Esson/Notebook/CHEM-581/2013/04/03: Difference between revisions
(One intermediate revision by the same user not shown) | |||
Line 60: | Line 60: | ||
<br> | <br> | ||
[[Image:50 PVA 146 NaMT micros diff.png]] | [[Image:50 PVA 146 NaMT micros diff.png]] | ||
*Fluorescence intensity maximum is | *Fluorescence intensity maximum is | ||
<br> | |||
Figure 5. Diffusion Testing of Rhodamine 6G in microspheres prepared with a 50:50 ratio PVA 146,000-186,000: 50% CEC NaMT | |||
<br> | |||
[[Image:50 PVA 146 50NaMT micros diff.png]] | |||
<br> | |||
*Fluorescence intensity maximum is 11.661 | |||
<br> | |||
Figure 6. Diffusion Testing of Rhodamine 6G in microspheres prepared with a 50:50 ratio PVA 146,000-186,000: 110% CEC Laponite | |||
<br> | |||
[[Image:50 PVA 146 110 LP.png]] | |||
<br> | |||
*Fluorescence intensity maximum is 137.319. | |||
<br> | |||
==Notes== | |||
* A tested "microspheres" more closely resemble smaller, more circular, more flexible hydrogels. Other microsphere samples were prepared and may more closely resemble microspheres. | |||
* The microsphere prepared with a 50:50 ratio PVA 146,000-186,000: 110% CEC Laponite caused the most diffusion of dye. All microspheres will be used for pressure testing, however, because not all dye leaked out. | |||
Revision as of 10:08, 7 April 2013
Project name | <html><img src="/images/9/94/Report.png" border="0" /></html> Main project page <html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>Previous entry<html> </html>Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html> |
Objectives
DecantingThe general protocol described on 2013/03/01 was followed.
DSC
Diffusion TestingA new general protocol for the preparation of was used for the diffusion testing of the prepared microspheres. It was determined that the previous protocol did not allow for a quantitative understanding of the amount of dye diffused from the samples.
Notes
|