(Observations for crosslinking films)
(fix raw html notebook nav)
 
(2 intermediate revisions by one other user not shown)
Line 2: Line 2:
 
|-
 
|-
 
|style="background-color: #EEE"|[[Image:owwnotebook_icon.png|128px]]<span style="font-size:22px;"> Project name</span>
 
|style="background-color: #EEE"|[[Image:owwnotebook_icon.png|128px]]<span style="font-size:22px;"> Project name</span>
|style="background-color: #F2F2F2" align="center"|<html><img src="/images/9/94/Report.png" border="0" /></html> [[{{#sub:{{FULLPAGENAME}}|0|-11}}|Main project page]]<br />{{#if:{{#lnpreventry:{{FULLPAGENAME}}}}|<html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>[[{{#lnpreventry:{{FULLPAGENAME}}}}{{!}}Previous entry]]<html>&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;</html>}}{{#if:{{#lnnextentry:{{FULLPAGENAME}}}}|[[{{#lnnextentry:{{FULLPAGENAME}}}}{{!}}Next entry]]<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html>}}
+
|style="background-color: #F2F2F2" align="center"|[[File:Report.png|frameless|link={{#sub:{{FULLPAGENAME}}|0|-11}}]][[{{#sub:{{FULLPAGENAME}}|0|-11}}|Main project page]]<br />{{#if:{{#lnpreventry:{{FULLPAGENAME}}}}|[[File:Resultset_previous.png|frameless|link={{#lnpreventry:{{FULLPAGENAME}}}}]][[{{#lnpreventry:{{FULLPAGENAME}}}}{{!}}Previous entry]]&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;}}{{#if:{{#lnnextentry:{{FULLPAGENAME}}}}|[[{{#lnnextentry:{{FULLPAGENAME}}}}{{!}}Next entry]][[File:Resultset_next.png|frameless|link={{#lnnextentry:{{FULLPAGENAME}}}}]]}}
 
|-
 
|-
 
| colspan="2"|
 
| colspan="2"|
Line 69: Line 69:
 
Please refer to [[User:Karlena_L._Brown/Notebook/CHEM-581/2012/10/26]] and [[User:Melissa_Novy/Notebook/CHEM-581/2012/10/26]] for calculations relating to preparation of higher concentration of porphyrin solutions and salt.
 
Please refer to [[User:Karlena_L._Brown/Notebook/CHEM-581/2012/10/26]] and [[User:Melissa_Novy/Notebook/CHEM-581/2012/10/26]] for calculations relating to preparation of higher concentration of porphyrin solutions and salt.
 
==AA==
 
==AA==
*Ran AA following the general protocol for atomic absorption. Ran on solutions collected from film adsorption completed [[User:Moira_M.Esson/Notebook/CHEM-581/2012/10/17/12|2012/10/17]]
+
*Ran AA following the general protocol for atomic absorption. Ran on solutions collected from film adsorption completed [[User:Moira_M._Esson/Notebook/CHEM-581/2012/10/17|2012/10/17]]
 
<br>
 
<br>
 
*Atomic Absorption Data
 
*Atomic Absorption Data

Latest revision as of 21:14, 26 September 2017

Owwnotebook icon.png Project name Report.pngMain project page
Resultset previous.pngPrevious entry      Next entryResultset next.png

Objectives

  1. Crosslink porphyrin films
  2. Run AA using film adsorption
  3. Prepare next highest porphyrin concentration solution. Then add salts to these higher porphyrin solutions


Crosslinking

  • The general protocol for porphyrin film crosslinking described on 2012/09/14 was followed for the films listed below


Films Crosslinked:

  1. PVOH(22K) 1.0073g+1.0mL GA+1mL porphyrin
  2. PVOH(22K) 1.05225g+1.0mL GA+1mL porphyrin


Crosslinking information

Films Amount of fixant solution used to crosslink(mL) Amount fixant solution kept in vial(mL) Amount of 1% aqueous HCl solution used to crosslink(mL Amount HCl solution saved in vial(mL) Amount of 0.2M sodium bicarbonate used(mL) Amount sodium bicarbonate solution saved(mL) Mass of film after crosslinking(g)
PVOH(22K) 1.0073g+1.0mL GA+1mL porphyrin 99.95 13 100 14 100 12 1.4974
PVOH(22K) 1.05225g+1.0mL GA+1mL porphyrin 101 12 98 13 99.8 12 1.9251
  • For the films listed below, the films were placed in a 6M NaCl solution at 70°C for ~1.5 hours

Crosslinked Films:

  1. PVOH(22K) 1.02114g+0.5mL GA+1mL porphyrin+HCl
  2. PVOH(22K) 1.0067g+1mL GA+1mL porphyrin+HCl


Crosslinking information:

Films crosslinked Amount of NaCl added(g) Amount 6M NaCl solution used(mL) Amount NaCl solution saved(mL) Mass of film after crosslinking(g)
PVOH(22K) 1.02114g+0.5mL GA+1mL porphyrin+HCl 0.3576 100 12 1.7781
PVOH(22K) 1.0067g+1mL GA+1mL porphyrin+HCl 0.363 99 12 1.5672

Observations for crosslinking films

  • PVOH(22K) 1.02114g+0.5mL GA+1mL porphyrin+HCl was shrunken, shriveled and was green in color before crosslinking
  • PVOH(22K) 1.0067g+1mL GA+1mL porphyrin+HCl shrunk, looked shriveled and was green in color before crosslinking
  • PVOH(22K) 1.0073g+1.0mL GA+1mL porphyrin was flat, relatively shiny and pink in color before crosslinking
  • PVOH(22K) 1.05225g+1.0mL GA+1mL porphyrin was flat, shiny and pink in color before crosslinking
  • When added film to fixant solution both beakers of solution had some color leak out. Color of both beakers were yellowish/greenish. Film with 1mL GA not as colored. Film with 0.5mL GA seems to be a more vibrant color(leaking more)
  • NaCl solution with film with 0.5mL GA had very slight leaking(slight discoloration of solution very light green). Coloration of solution was occurring very gradually
  • Both films after fixant solution were a vibrant green color(like jolly rancher green). Film with 1.0mL GA was a darker/ more vibrant green
  • Films placed in 1% aqueous HCl soltn. both started to have color leak out
  • 1.0mL GA+HCl film when placed in the 6M NaCl solution leaked very minimally(solution looks very faintly green). Much less in comparison to 0.5mL GA.
  • 0.5mL GA+HCl film after 1hr. and 15min. heated , remained bright green color. Stored in H2O. After adding H2O, film turned into a pink color(darker pink on edges)
  • Addition of both films to sodium bicarbonate caused all porphyrin to leak out(films no longer colored. completely clear.)
  • Film 1mLGA+HCl remained dark green and more stiff than other film. Turned pink after addition to deionized H2O


Please refer to User:Karlena_L._Brown/Notebook/CHEM-581/2012/10/26 and User:Melissa_Novy/Notebook/CHEM-581/2012/10/26 for calculations relating to preparation of higher concentration of porphyrin solutions and salt.

AA

  • Ran AA following the general protocol for atomic absorption. Ran on solutions collected from film adsorption completed 2012/10/17


  • Atomic Absorption Data
' Concentration [ppm] Abs. [ ] BG '
0.01 -0.00600 0.00200
0.05 -0.01160 0.00540
1 -0.00920 0.00150
2 0.11710 0.00470
3 0.20330 0.00330
Given Conc. [ppm] Abs. [ ] BG Conc. [ppm]
1 min NaMT-CuSO4 7.4 0.37690 0.00430 5.63990
10 0.47600 0.00620 7.01910
5 min NaMT-CuSO4 7.4 0.38080 0.00350 5.69420
10 0.48150 0.00600 7.09560
10 min NaMT-CuSO4 7.4 0.29540 0.00370 4.50580
10 0.37640 0.00480 5.63300
1 min 100%CEC NaMT-CuSO4 7.4 0.48030 0.00680 7.07890
10 0.61880 0.00950 9.00630
5 min 100%CEC NaMT-CuSO4 7.4 0.46120 0.00640 6.81310
10 0.62080 0.00790 9.03420
10 min 100%CEC NaMT-CuSO4 7.4 0.43300 0.00400 6.42070
10 0.62960 0.00480 9.15660
1 min 50%CEC NaMT-CuSO4 7.4 0.47470 0.00530 7.00100
10 0.62050 0.00490 9.03000
5 min 50%CEC NaMT-CuSO4 7.4 0.46110 0.00310 6.81170
10 0.60940 0.00580 8.87550
10 min 50%CEC NaMT-CuSO4 7.4 0.46800 0.00390 6.90770
10 0.59620 0.00440 8.69180