Difference between revisions of "User:Mobeen Ashraf/Notebook/Chem-581/2012/10/03"

From OpenWetWare
Jump to: navigation, search
(Autocreate 2012/10/03 Entry for User:Mobeen_Ashraf/Notebook/Chem-581)
 
(fix raw html notebook nav)
 
(7 intermediate revisions by one other user not shown)
Line 2: Line 2:
 
|-
 
|-
 
|style="background-color: #EEE"|[[Image:BDLlogo_notext_lr.png|128px]]<span style="font-size:22px;"> Experimental Chemistry</span>
 
|style="background-color: #EEE"|[[Image:BDLlogo_notext_lr.png|128px]]<span style="font-size:22px;"> Experimental Chemistry</span>
|style="background-color: #F2F2F2" align="center"|<html><img src="/images/9/94/Report.png" border="0" /></html> [[{{#sub:{{FULLPAGENAME}}|0|-11}}|Main project page]]<br />{{#if:{{#lnpreventry:{{FULLPAGENAME}}}}|<html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>[[{{#lnpreventry:{{FULLPAGENAME}}}}{{!}}Previous entry]]<html>&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;</html>}}{{#if:{{#lnnextentry:{{FULLPAGENAME}}}}|[[{{#lnnextentry:{{FULLPAGENAME}}}}{{!}}Next entry]]<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html>}}
+
|style="background-color: #F2F2F2" align="center"|[[File:Report.png|frameless|link={{#sub:{{FULLPAGENAME}}|0|-11}}]][[{{#sub:{{FULLPAGENAME}}|0|-11}}|Main project page]]<br />{{#if:{{#lnpreventry:{{FULLPAGENAME}}}}|[[File:Resultset_previous.png|frameless|link={{#lnpreventry:{{FULLPAGENAME}}}}]][[{{#lnpreventry:{{FULLPAGENAME}}}}{{!}}Previous entry]]&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;}}{{#if:{{#lnnextentry:{{FULLPAGENAME}}}}|[[{{#lnnextentry:{{FULLPAGENAME}}}}{{!}}Next entry]][[File:Resultset_next.png|frameless|link={{#lnnextentry:{{FULLPAGENAME}}}}]]}}
 
|-
 
|-
 
| colspan="2"|
 
| colspan="2"|
Line 10: Line 10:
  
 
==Objective==
 
==Objective==
 +
 +
DMA- Dynamic Mechanical Analysis on PVOH films
  
 
==Description==
 
==Description==
 +
 +
Following PVOH Films were Cross-linked:
 +
 +
*1) PVOH film, MW of 22,000-placed in an oven set at 120 deg Celsius for 90 mins.
 +
*2) PVOH film, MW of 100,000-placed in an oven set at 120 deg Celsius for 90 mins.
 +
*3) PVOH film, MW of 100,000 cross-linked with HCl-placed in an oven set at 120 deg Celsius for 90 mins.
 +
*4) PVOH film, MW of 22,000, cross-linked H3PO4-placed in an oven set at 120 deg Celsius for 90 mins.
 +
*5) PVOH film, MW of 22,000, cross-linked with maleic acid and H3PO4-placed in an oven set at 120 deg Celsius for 90 mins.
 +
 +
'''DMA Analysis:'''
 +
 +
PVOH films were subject to stretch( elastic tension ) mechanical analysis to test its mechanical durability.
 +
 +
* PVOH (film 1) was selected for DMA analysis. By using vernier calipers, the height and width of the film was measured to be 20.49 mm and 0.22 mm respectively.
  
 
==Data==
 
==Data==
 
* Add data and results here...
 
* Add data and results here...
 +
 +
The films that were cross-linked in the oven had some considerable changes in color and toughness:
 +
 +
*PVOH MW 100,000- film was firmer and there was no apparent color change.
 +
 +
*PVOH MW 22000- no apparent color and physical change that was observed.
 +
 +
*PVOH MW 22000 cross linked with H3PO4- film became much tougher and turned a slight yellowish brown color.
 +
 +
*PVOH MW 22000 with H3PO4 and maleic acid- no apparent color and physical change that was observed.
 +
 +
*PVOH MW 100,000 cross-linked w/ hydrochloric acid- slightly firm, but color change was very prominent- dark, jet blackish.
  
 
==Notes==
 
==Notes==

Latest revision as of 21:13, 26 September 2017

BDLlogo notext lr.png Experimental Chemistry Report.pngMain project page
Resultset previous.pngPrevious entry      Next entryResultset next.png


Objective

DMA- Dynamic Mechanical Analysis on PVOH films

Description

Following PVOH Films were Cross-linked:

  • 1) PVOH film, MW of 22,000-placed in an oven set at 120 deg Celsius for 90 mins.
  • 2) PVOH film, MW of 100,000-placed in an oven set at 120 deg Celsius for 90 mins.
  • 3) PVOH film, MW of 100,000 cross-linked with HCl-placed in an oven set at 120 deg Celsius for 90 mins.
  • 4) PVOH film, MW of 22,000, cross-linked H3PO4-placed in an oven set at 120 deg Celsius for 90 mins.
  • 5) PVOH film, MW of 22,000, cross-linked with maleic acid and H3PO4-placed in an oven set at 120 deg Celsius for 90 mins.

DMA Analysis:

PVOH films were subject to stretch( elastic tension ) mechanical analysis to test its mechanical durability.

  • PVOH (film 1) was selected for DMA analysis. By using vernier calipers, the height and width of the film was measured to be 20.49 mm and 0.22 mm respectively.

Data

  • Add data and results here...

The films that were cross-linked in the oven had some considerable changes in color and toughness:

*PVOH MW 100,000- film was firmer and there was no apparent color change.
*PVOH MW 22000- no apparent color and physical change that was observed.
*PVOH MW 22000 cross linked with H3PO4- film became much tougher and turned a slight yellowish brown color.
*PVOH MW 22000 with H3PO4 and maleic acid- no apparent color and physical change that was observed.
*PVOH MW 100,000 cross-linked w/ hydrochloric acid- slightly firm, but color change was very prominent- dark, jet blackish.