Difference between revisions of "User:Melissa Novy/Notebook/CHEM-572/2013/04/03"

From OpenWetWare
< User:Melissa Novy‎ | Notebook‎ | CHEM-572‎ | 2013‎ | 04
Jump to: navigation, search
(Autocreate 2013/04/03 Entry for User:Melissa_Novy/Notebook/CHEM-572)
 
(fix raw html help text)
 
(One intermediate revision by one other user not shown)
Line 10: Line 10:
 
<!-- ## END search column  ## -->
 
<!-- ## END search column  ## -->
 
|-  
 
|-  
|colspan="2" style="background-color: #F2F2F2;" align="right"|[[{{FULLPAGENAME}}/Entry_Base|Customize your entry pages]] [[Help:Notebook/Project_Base/Customize_entry_page|<html><img src="/images/a/aa/Help.png" border="0" /></html>]]
+
|colspan="2" style="background-color: #F2F2F2;" align="right"|[[{{FULLPAGENAME}}/Entry_Base|Customize your entry pages]] [[Image:Help.png|frameless|link=Help:Notebook/Project_Base/Customize_entry_page]]
 
|-  
 
|-  
 
|colspan="2"|
 
|colspan="2"|
 
<!-- ##### DO NOT edit above this line unless you know what you are doing. ##### -->
 
<!-- ##### DO NOT edit above this line unless you know what you are doing. ##### -->
  
==Entry title==
+
==Objectives==
* Insert content here...
+
* Filter more 100AgLMT.
 +
* Make films of PLA2002D + 33wt% LMT and PLA2002D + 33wt% 100AgLMT.
 +
 
 +
==100AgLMT==
 +
* The reserved gel of 100AgLMT, made on [[User:Melissa_Novy/Notebook/CHEM-572/2013/02/12|2013/02/12]], was filtered with 42 Whatman paper and washed with 3 10-mL aliquots of (50:50) H<sub>2</sub>O/EtOH.  Afterward, the clay was placed in an aluminum dish in an 80°C oven to dry overnight.  It was subsequently ground with a mortar and pestle for use in films.
 +
 
 +
==PLA2002D Films==
 +
* The protocol on [[User:Melissa_Novy/Notebook/CHEM-572/2013/02/06|2013/02/06]] was followed to make both films.
 +
<br>
 +
 
 +
PLA2002D + 33wt% LMT
 +
* Theoretical mass PLA2002D: 3.00 g
 +
** Actual mass PLA2002D: 3.01 g
 +
* Theoretical mass LMT: 1.02206 g
 +
** Actual mass LMT: 1.00121 g
 +
<br>
 +
 
 +
PLA2002D + 33wt% 100AgLMT
 +
* Theoretical mass PLA2002D: 3.00 g
 +
** Actual mass PLA2002D: 3.00 g
 +
* Theoretical mass 100AgLMT: 1.02206 g
 +
** Actual mass 100AgLMT: 0.52178 g
 +
<br>
 +
 
 +
* Note that there was not enough 100AgLMT remaining to achieve 1.02206 g of sample. The final amount of 100AgLMT in the film was 17% of the 3 g of polymer.
  
  

Latest revision as of 18:32, 23 September 2017

<!-- sibboleth --><div id="lncal1" style="border:0px;"><div style="display:none;" id="id">lncal1</div><div style="display:none;" id="dtext"></div><div style="display:none;" id="page">User:Melissa Novy/Notebook/CHEM-572/2013/04/03</div><div style="display:none;" id="fmt">yyyy/MM/dd</div><div style="display:none;" id="css">OWWNB</div><div style="display:none;" id="month"></div><div style="display:none;" id="year"></div><div style="display:none;" id="readonly">Y</div></div>

BDLlogo 300.png <sitesearch>title=Search this Project</sitesearch>

Customize your entry pages Help.png

Objectives

  • Filter more 100AgLMT.
  • Make films of PLA2002D + 33wt% LMT and PLA2002D + 33wt% 100AgLMT.

100AgLMT

  • The reserved gel of 100AgLMT, made on 2013/02/12, was filtered with 42 Whatman paper and washed with 3 10-mL aliquots of (50:50) H2O/EtOH. Afterward, the clay was placed in an aluminum dish in an 80°C oven to dry overnight. It was subsequently ground with a mortar and pestle for use in films.

PLA2002D Films

  • The protocol on 2013/02/06 was followed to make both films.


PLA2002D + 33wt% LMT

  • Theoretical mass PLA2002D: 3.00 g
    • Actual mass PLA2002D: 3.01 g
  • Theoretical mass LMT: 1.02206 g
    • Actual mass LMT: 1.00121 g


PLA2002D + 33wt% 100AgLMT

  • Theoretical mass PLA2002D: 3.00 g
    • Actual mass PLA2002D: 3.00 g
  • Theoretical mass 100AgLMT: 1.02206 g
    • Actual mass 100AgLMT: 0.52178 g


  • Note that there was not enough 100AgLMT remaining to achieve 1.02206 g of sample. The final amount of 100AgLMT in the film was 17% of the 3 g of polymer.