==Procedure==
 
==Procedure==
* 3.45g of AgNO<sub>3</sub> was weighted out and placed in a 50mL Erylenmeyer flask.  
+
* 2.87g of AgNO<sub>3</sub> was weighted out and placed in a 50mL Erylenmeyer flask.  
* 0.8g of Laponite clay was weighted out and placed in same Erlenmeyer flask as above.
+
* 0.3g of Laponite clay was weighted out and placed in same Erlenmeyer flask as above.
* The 0.8g of Laponite clay was calculated in the following ways:
+
* The 2.87g of AgNO<sub>3</sub> was calculated in the following ways:
 
   Cationic exchange capacity of Laponite: 0.55 milliequivilient/gram
 
   Cationic exchange capacity of Laponite: 0.55 milliequivilient/gram
 
   Weight % of silver to be exchanged in Clay: 95%
 
   Weight % of silver to be exchanged in Clay: 95%
 
   Calculation is shown as follows:
 
   Calculation is shown as follows:
   ___________
+
   0.3 g LMT × (55 meqv/100 g LMT) × (1 mol Ag<sup>+</sup>/1000 meqv) × (107.86 g Ag<sup>+</sup>/1 mol Ag<sup>+</sup>) × (1 mol Ag<sup>+</sup>/1 mol AgNO<sub>3</sub>) × (1 mol AgNO<sub>3</sub>/169.87 g AgNO<sub>3</sub>) × 95% = 0.00009953 g AgNO<sub>3</sub>
 
* 10mL of 50/50 water/ethanol solution was made by combining 5mL of water and 5mL of ethanol in a 10mL graduated cylinder.
 
* 10mL of 50/50 water/ethanol solution was made by combining 5mL of water and 5mL of ethanol in a 10mL graduated cylinder.
 
* 10mL of water/ethanol solution was poured into Erylenmeyer flask along with a stir bar.
 
* 10mL of water/ethanol solution was poured into Erylenmeyer flask along with a stir bar.
* The Erylenmeyer flask containing the solution is placed on stir plate for 24 hours.
+
* The Erylenmeyer flask containing the solution is covered with aluminum foil and placed on stir plate under fume hood for 24 hours.
 +
 
 +
==Observations==
 +
* The clay and AgNO<sub>3</sub> solution appeared white in color during stirring.
 
    
 
    
  

Revision as of 10:53, 5 February 2013

Owwnotebook icon.png Experimental Biochemistry II <html><img src="/images/9/94/Report.png" border="0" /></html> Main project page
<html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>Previous entry<html>&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;</html>Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html>

Purpose

  • Start making sample Silver film with proposed protocol

Procedure

  • 2.87g of AgNO3 was weighted out and placed in a 50mL Erylenmeyer flask.
  • 0.3g of Laponite clay was weighted out and placed in same Erlenmeyer flask as above.
  • The 2.87g of AgNO3 was calculated in the following ways:
  Cationic exchange capacity of Laponite: 0.55 milliequivilient/gram
  Weight % of silver to be exchanged in Clay: 95%
  Calculation is shown as follows:
  0.3 g LMT × (55 meqv/100 g LMT) × (1 mol Ag+/1000 meqv) × (107.86 g Ag+/1 mol Ag+) × (1 mol Ag+/1 mol AgNO3) × (1 mol AgNO3/169.87 g AgNO3) × 95% = 0.00009953 g AgNO3
  • 10mL of 50/50 water/ethanol solution was made by combining 5mL of water and 5mL of ethanol in a 10mL graduated cylinder.
  • 10mL of water/ethanol solution was poured into Erylenmeyer flask along with a stir bar.
  • The Erylenmeyer flask containing the solution is covered with aluminum foil and placed on stir plate under fume hood for 24 hours.

Observations

  • The clay and AgNO3 solution appeared white in color during stirring.