Difference between revisions of "User:Karlena L. Brown/Notebook/PVOH Research/2013/04/03"

From OpenWetWare
Jump to: navigation, search
(Fluorescence Analysis: Diffusion Testing 2)
(Fluorescence Analysis: Diffusion Testing 2)
Line 43: Line 43:
 
   # Microsphere 90:10 PVOH 146K 110% CEC Laponite w/ DMHXLBR
 
   # Microsphere 90:10 PVOH 146K 110% CEC Laponite w/ DMHXLBR
 
   # Microsphere 90:10 PVOH 146K NaMT
 
   # Microsphere 90:10 PVOH 146K NaMT
   # Microsphere 50:50 PVOH 146K CEC NaMT w/ Bu<sub>3</sub>HdP<sup>+</sup>
+
   # Microsphere 50:50 PVOH 146K NaMT
 +
  # Microsphere 50:50 PVOH 146K 50% CEC NaMT w/ Bu<sub>3</sub>HdP<sup>+</sup>
 
   # Microsphere 50:50 PVOH 146K 110% CEC Laponite w/ DMHXLBR
 
   # Microsphere 50:50 PVOH 146K 110% CEC Laponite w/ DMHXLBR
  
Line 52: Line 53:
 
     # Emission Slit Width: 10
 
     # Emission Slit Width: 10
 
     # Scan Speed: 1200
 
     # Scan Speed: 1200
 +
 +
==Fluorescence Results & Spectrums==
 +
 +
<br>
 +
Figure 1 - Microsphere 90:10 PVOH 146K 50% CEC NaMT w/ Bu<sub>3</sub>HdP<sup>+</sup>
 +
<br>
 +
[[Image:90 pva 146 50NaMT micros diffusion.jpg]]
 +
<br>
 +
***Fluorescence intensity maximum is 6.985
 +
 +
<br>
 +
Figure 2 - Microsphere 90:10 PVOH 146K 110% CEC Laponite w/ DMHXLBR
 +
<br>
 +
[[Image:90 PVA 146 110LP micros diff.jpg]]
 +
<br>
 +
***Fluorescence intensity maximum is 5.109
 +
 +
<br>
 +
Figure 3 - Microsphere 90:10 PVOH 146K NaMT
 +
<br>
 +
[[Image:90 PVA 146 NaMT micros diff test.png]]
 +
<br>
 +
***Fluorescence intensity maximum is 26.734
 +
 +
<br>
 +
Figure 4 - Microsphere 50:50 PVOH 146K NaMT
 +
<br>
 +
[[Image:50 PVA 146 NaMT micros diff.png]]
 +
***Fluorescence intensity maximum is 17.
 +
 +
<br>
 +
Figure 5 - Microsphere 50:50 PVOH 146K 50% CEC NaMT w/ Bu<sub>3</sub>HdP<sup>+</sup>
 +
<br>
 +
[[Image:50 PVA 146 50NaMT micros diff.png]]
 +
<br>
 +
***Fluorescence intensity maximum is 11.661
 +
<br>
 +
 +
Figure 6 - Microsphere 50:50 PVOH 146K 110% CEC Laponite w/ DMHXLBR
 +
<br>
 +
[[Image:50 PVA 146 110 LP.png]]
 +
<br>
 +
***Fluorescence intensity maximum is 137.319.
 +
<br>
  
 
==Notes==
 
==Notes==

Revision as of 19:38, 8 April 2013

Owwnotebook icon.png PVOH Research <html><img src="/images/9/94/Report.png" border="0" /></html> Main project page
<html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>Previous entry<html>&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;</html>Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html>

OBJECTIVES

  • Collect all DSC results from dry clay samples previously prepared on 2/08/13
  • Run DSC sample analysis on dry clay samples previously prepared on 3/29/13
  • Remove all excess oil from controlled microsphere samples prepared on 03/29/13
  • Run fluorescence analysis on all microsphere samples prepared 02/20/13 with Rhodamine 6G dye

DSC Results for Dry Clay Samples

DSC Analysis: Mixed Microspheres

DSC preparation and protocol involving instrumentation and usage can be found on 9/17/12 entry.

Sample Name Sample Mass (mg) Pan / Lid Mass (mg)
50:50 PVOH 130K NaMT 3.12 50.01
90:10 PVOH 130K 110% CEC NaMT w/ DMHXLBR 2.29 50.17
90:10 PVOH 130K Laponite 2.59 50.12
90:10 PVOH 130K 110% CEC Laponite w/ DMHXLBR 2.27 50.28
90:10 PVOH 146K 110% CEC NaMT w/ DMHXLBR 2.65 50.11
50:50 PVOH 146K 110% CEC NaMT w/ DMHXLBR 2.50 50.17

Fluorescence Analysis: Diffusion Testing 2

RECALL DIFFUSION TESTING PROTOCOL ON 2/15/13

  • Fluorescent samples run and completed for 2hr diffusion rate determinations:
  # Microsphere 90:10 PVOH 146K 50% CEC NaMT w/ Bu3HdP+
  # Microsphere 90:10 PVOH 146K 110% CEC Laponite w/ DMHXLBR
  # Microsphere 90:10 PVOH 146K NaMT
  # Microsphere 50:50 PVOH 146K NaMT
  # Microsphere 50:50 PVOH 146K 50% CEC NaMT w/ Bu3HdP+
  # Microsphere 50:50 PVOH 146K 110% CEC Laponite w/ DMHXLBR
  • Specific parameters used to analyze fluorescence of hydrogel samples containing Rhodamine 6G dye included the following:
    # Excitation: 480nm
    # Emission Range: 500-650nm
    # Excitation Slit Width: 10
    # Emission Slit Width: 10
    # Scan Speed: 1200

Fluorescence Results & Spectrums


Figure 1 - Microsphere 90:10 PVOH 146K 50% CEC NaMT w/ Bu3HdP+
90 pva 146 50NaMT micros diffusion.jpg

      • Fluorescence intensity maximum is 6.985


Figure 2 - Microsphere 90:10 PVOH 146K 110% CEC Laponite w/ DMHXLBR
90 PVA 146 110LP micros diff.jpg

      • Fluorescence intensity maximum is 5.109


Figure 3 - Microsphere 90:10 PVOH 146K NaMT
90 PVA 146 NaMT micros diff test.png

      • Fluorescence intensity maximum is 26.734


Figure 4 - Microsphere 50:50 PVOH 146K NaMT
50 PVA 146 NaMT micros diff.png

      • Fluorescence intensity maximum is 17.


Figure 5 - Microsphere 50:50 PVOH 146K 50% CEC NaMT w/ Bu3HdP+
50 PVA 146 50NaMT micros diff.png

      • Fluorescence intensity maximum is 11.661


Figure 6 - Microsphere 50:50 PVOH 146K 110% CEC Laponite w/ DMHXLBR
50 PVA 146 110 LP.png

      • Fluorescence intensity maximum is 137.319.


Notes