== | ==OBJECTIVES== | ||
''' | * Collect all DSC results from dry clay samples previously prepared on '''2/08/13''' | ||
* | * Run DSC sample analysis on dry clay samples previously prepared on '''3/29/13''' | ||
''' | * Remove all excess oil from controlled microsphere samples prepared on '''03/29/13''' | ||
* | * Run fluorescence analysis on all microsphere samples prepared '''02/20/13''' with Rhodamine 6G dye | ||
* | |||
''' | |||
==DSC Results for Dry Clay Samples== | |||
''' | |||
==DSC Analysis: Mixed Microspheres== | |||
'''DSC preparation and protocol involving instrumentation and usage can be found on 9/17/12 entry.''' | |||
* | |||
{| {{table}} | |||
| align="center" style="background:#f0f0f0;"|'''Sample Name''' | |||
| align="center" style="background:#f0f0f0;"|'''Sample Mass (mg)''' | |||
| align="center" style="background:#f0f0f0;"|'''Pan / Lid Mass (mg)''' | |||
|- | |||
| 50:50 PVOH 130K NaMT||3.12||50.01 | |||
|- | |||
| 90:10 PVOH 130K 110% CEC NaMT w/ DMHXLBR||2.29||50.17 | |||
|- | |||
| 90:10 PVOH 130K Laponite||2.59||50.12 | |||
|- | |||
| 90:10 PVOH 130K 110% CEC Laponite w/ DMHXLBR||2.27||50.28 | |||
|- | |||
| 90:10 PVOH 146K 110% CEC NaMT w/ DMHXLBR||2.65||50.11 | |||
|- | |||
| 50:50 PVOH 146K 110% CEC NaMT w/ DMHXLBR||2.50||50.17 | |||
|} | |||
==Fluorescence Analysis: Diffusion Testing 2== | |||
'''RECALL DIFFUSION TESTING PROTOCOL ON 2/13/13''' | |||
* Fluorescent samples run and completed for 2hr diffusion rate determinations: | |||
# Microsphere 90:10 PVOH 146K 50% CEC NaMT w/ Bu<sub>3</sub>HdP<sup>+</sup> | |||
# Microsphere 90:10 PVOH 146K 110% CEC Laponite w/ DMHXLBR | |||
# Microsphere 90:10 PVOH 146K NaMT | |||
# Microsphere 50:50 PVOH 146K CEC NaMT w/ Bu<sub>3</sub>HdP<sup>+</sup> | |||
# Microsphere 50:50 PVOH 146K 110% CEC Laponite w/ DMHXLBR | |||
* Specific parameters used to analyze fluorescence of hydrogel samples containing Rhodamine 6G dye included the following: | |||
# Excitation: 480nm | |||
# Emission Range: 500-650nm | |||
# Excitation Slit Width: 10 | |||
# Emission Slit Width: 10 | |||
# Scan Speed: 1200 | |||
==Notes== | |||
Revision as of 20:08, 8 April 2013
PVOH Research | <html><img src="/images/9/94/Report.png" border="0" /></html> Main project page <html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>Previous entry<html> </html>Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html> | |||||||||||||||||||||
OBJECTIVES
DSC Results for Dry Clay SamplesDSC Analysis: Mixed MicrospheresDSC preparation and protocol involving instrumentation and usage can be found on 9/17/12 entry.
Fluorescence Analysis: Diffusion Testing 2RECALL DIFFUSION TESTING PROTOCOL ON 2/13/13
# Microsphere 90:10 PVOH 146K 50% CEC NaMT w/ Bu3HdP+ # Microsphere 90:10 PVOH 146K 110% CEC Laponite w/ DMHXLBR # Microsphere 90:10 PVOH 146K NaMT # Microsphere 50:50 PVOH 146K CEC NaMT w/ Bu3HdP+ # Microsphere 50:50 PVOH 146K 110% CEC Laponite w/ DMHXLBR
# Excitation: 480nm # Emission Range: 500-650nm # Excitation Slit Width: 10 # Emission Slit Width: 10 # Scan Speed: 1200 Notes |