==OBJECTIVES==
 
==OBJECTIVES==
# Continue fluorescence detection through pressure testing analysis of hydrogel samples (new modifications & better results)
+
* Continue fluorescence detection through pressure testing analysis of hydrogel samples (new modifications & better results)
  
 
==Hydrogel Pressure Samples Tested 2==
 
==Hydrogel Pressure Samples Tested 2==

Revision as of 13:02, 24 March 2013

Owwnotebook icon.png PVOH Research <html><img src="/images/9/94/Report.png" border="0" /></html> Main project page
<html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>Previous entry<html>      </html>Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html>

OBJECTIVES

  • Continue fluorescence detection through pressure testing analysis of hydrogel samples (new modifications & better results)

Hydrogel Pressure Samples Tested 2

RECALL HYDROGEL PRESSURE TESTING PROTOCOL ON 2/20/13 & FLUORESCENCE ANALYSIS PROCEDURES ON 2/13/13

Sample Order PVOH vs. Clay Ratio PVOH Type Clay Selection Amount of Hydrogel Used (g)
1 90:10 146K 110% CEC NaMT w/ DMHXLBR 0.1084
2 90:10 130K NaMT 0.1044
3 50:50 146K 110% CEC NaMT w/ DMHXLBR 0.1092
4 90:10 130K 110% CEC Laponite w/ DMHXLBR 0.1050
5 50:50 130K NaMT 0.1050
6 90:10 130K Laponite 0.1015
7 50:50 146K 110% CEC Laponite w/ DMHXLBR 0.1080
8 50:50 130K Laponite 0.1036
9 90:10 130K 110% CEC NaMT w/ DMHXLBR 0.1011
10 50:50 130K 110% CEC Laponite w/ DMHXLBR 0.1036
11 90:10 130K 110% CEC NaMT w/ DMHXLBR 0.1011
12 90:10 146K Laponite 0.1026
13 50:50 130K 50% CEC NaMT w/ Bu3HdP+ 0.1052
14 50:50 146K Laponite 0.1045
15 90:10 130K 50% CEC NaMT w/ Bu3HdP+ 0.1145

Notes

  • The pipettes that provided the best fluorescence results for each sample were both the straight plastic pipette and 90° angle bent pipette
  • All samples run maintained a composition incorporating Rhodamine 6G dye
  • In comparison, the laponite incorporated hydrogels are squishy, clear, extremely adsorbent, and soft to touch
  • The sodium montmorrillonite incorporated hydrogels are hard, dingy, flat, and dull colored (brownish appearance)
  • For laponite samples, one can actually see the Rhodamine 6G dye added clearly within each hydrogel sample (reddish pink appearance)
  • Also the sodium montmorrillonite samples in most cases began to grow a greenish type mold within the hydrogels
  • All samples on 2/27/13 were tested using the bent pipette containing the 90° angle (See figure listed below)

Figure 1. Image of bent pipette used for pressure testing Bent pipette 2 27 13.jpg