==OBJECTIVES==
 
==OBJECTIVES==
 
==Hydrogel Pressure Samples Tested==
 
==Hydrogel Pressure Samples Tested==
 +
'''RECALL HYDROGEL PRESSURE TESTING PROTOCOL ON 2/20/13 & FLUORESCENCE ANALYSIS PROCEDURES ON 2/13/13'''
 +
 +
{| {{table}}
 +
| align="center" style="background:#f0f0f0;"|'''Sample Order'''
 +
| align="center" style="background:#f0f0f0;"|'''PVOH vs. Clay Ratio'''
 +
| align="center" style="background:#f0f0f0;"|'''PVOH Type'''
 +
| align="center" style="background:#f0f0f0;"|'''Clay Selection'''
 +
| align="center" style="background:#f0f0f0;"|'''Amount of Hydrogel Used (g)'''
 +
|-
 +
| 1||90:10||146K||110% CEC NaMT w/ DMHXLBR||0.1084
 +
|-
 +
| 2||90:10||130K||NaMT||0.1044
 +
|-
 +
| 3||50:50||146K||110% CEC NaMT w/ DMHXLBR||0.1092
 +
|-
 +
| 4||90:10||130K||110% CEC Laponite w/ DMHXLBR||0.1050
 +
|-
 +
| 5||50:50||130K||NaMT||0.1050
 +
|-
 +
| 6||90:10||130K||Laponite||0.1015
 +
|-
 +
| 7||50:50||146K||110% CEC Laponite w/ DMHXLBR||0.1080
 +
|-
 +
| 8||50:50||130K||Laponite||0.1036
 +
|-
 +
| 9||90:10||130K||110% CEC NaMT w/ DMHXLBR||0.1011
 +
|-
 +
| 10||50:50||130K||110% CEC Laponite w/ DMHXLBR||0.1036
 +
|-
 +
| 11||90:10||130K||110% CEC NaMT w/ DMHXLBR||0.1011
 +
|-
 +
| 12||90:10||146K||Laponite||0.1026
 +
|-
 +
| 13||50:50||130K||50% CEC NaMT w/ Bu<sub>3</sub>HdP<sup>+</sup>||0.1052
 +
|-
 +
| 14||50:50||146K||Laponite||0.1045
 +
|-
 +
| 15||90:10||130K||50% CEC NaMT w/ Bu<sub>3</sub>HdP<sup>+</sup>||0.1145
 +
|}
 +
 
==Notes==
 
==Notes==
 
* The pipettes that provided the best fluorescence results for each sample were both the straight plastic pipette and 90° angle bent pipette.
 
* The pipettes that provided the best fluorescence results for each sample were both the straight plastic pipette and 90° angle bent pipette.

Revision as of 19:55, 4 March 2013

Owwnotebook icon.png PVOH Research <html><img src="/images/9/94/Report.png" border="0" /></html> Main project page
<html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>Previous entry<html>&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;</html>Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html>

OBJECTIVES

Hydrogel Pressure Samples Tested

RECALL HYDROGEL PRESSURE TESTING PROTOCOL ON 2/20/13 & FLUORESCENCE ANALYSIS PROCEDURES ON 2/13/13

Sample Order PVOH vs. Clay Ratio PVOH Type Clay Selection Amount of Hydrogel Used (g)
1 90:10 146K 110% CEC NaMT w/ DMHXLBR 0.1084
2 90:10 130K NaMT 0.1044
3 50:50 146K 110% CEC NaMT w/ DMHXLBR 0.1092
4 90:10 130K 110% CEC Laponite w/ DMHXLBR 0.1050
5 50:50 130K NaMT 0.1050
6 90:10 130K Laponite 0.1015
7 50:50 146K 110% CEC Laponite w/ DMHXLBR 0.1080
8 50:50 130K Laponite 0.1036
9 90:10 130K 110% CEC NaMT w/ DMHXLBR 0.1011
10 50:50 130K 110% CEC Laponite w/ DMHXLBR 0.1036
11 90:10 130K 110% CEC NaMT w/ DMHXLBR 0.1011
12 90:10 146K Laponite 0.1026
13 50:50 130K 50% CEC NaMT w/ Bu3HdP+ 0.1052
14 50:50 146K Laponite 0.1045
15 90:10 130K 50% CEC NaMT w/ Bu3HdP+ 0.1145

Notes

  • The pipettes that provided the best fluorescence results for each sample were both the straight plastic pipette and 90° angle bent pipette.
  • All samples run maintained a composition incorporating Rhodamine 6G dye
  • All samples on 2/27/13 were tested using the bent pipette containing the 90° angle. (See figure listed below)

Figure 1. Image of bent pipette used for pressure testing Bent pipette 2 27 13.jpg