(Microsphere PVOH 146K 110% CEC Laponite w/ DMHXLBR Information)
(Microsphere PVOH 146K 110% CEC Laponite w/ DMHXLBR Information)
Line 13: Line 13:
 
==Microsphere PVOH 146K 110% CEC Laponite w/ DMHXLBR Information==
 
==Microsphere PVOH 146K 110% CEC Laponite w/ DMHXLBR Information==
 
{| {{table}}
 
{| {{table}}
| align="center" style="background:#f0f0f0;"|'''Preparation of Microspheres using PVA MW 146,000-186,000'''
+
| align="center" style="background:#f0f0f0;"|'''Preparation of 110% Laponite Microspheres using PVOH MW 146,000-186,000'''
 
| align="center" style="background:#f0f0f0;"|''''''
 
| align="center" style="background:#f0f0f0;"|''''''
 
|-
 
|-
| PVOH 146K added(g)||0.9001
+
| PVOH 146K added(g)||0.9005
 
|-
 
|-
| Laponite clay added (g)||0.1004
+
| 110% Laponite clay added (g)||0.1002
 
|-
 
|-
| Cellulose Acetate Butyrate added (g)||0.6066
+
| Cellulose Acetate Butyrate added (g)||0.6001
 
|-
 
|-
 
| Glutaraldehyde added (mL)||0.75
 
| Glutaraldehyde added (mL)||0.75

Revision as of 22:46, 10 February 2013

Owwnotebook icon.png PVOH Research <html><img src="/images/9/94/Report.png" border="0" /></html> Main project page
<html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>Previous entry<html>      </html>Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html>

OBJECTIVES

  • Continue preparing polyvinyl alcohol microspheres for experimental analysis
  • Dilute Rhodamine 6G dye solution down to 1μM concentration for prepared microspheres
  • Prepare DSC samples for polyvinyl alcohol microspheres created

Microsphere PVOH 146K 110% CEC Laponite w/ DMHXLBR Information

Preparation of 110% Laponite Microspheres using PVOH MW 146,000-186,000 '
PVOH 146K added(g) 0.9005
110% Laponite clay added (g) 0.1002
Cellulose Acetate Butyrate added (g) 0.6001
Glutaraldehyde added (mL) 0.75
H2SO4 added (mL) 0.25


Rhodamine 6G Dye Dilution Calculations

1μM Rhodamine 6G Dye Concentration

  M1V1 = M2V2
  1μM (RG6)x 25mL = (92μM)V2    V2 = 271.74μL

DSC Analysis: Exchanged Clays & PVOH 146K Microspheres

DSC preparation and protocal involving instrumentation and usage can be found on 9/17/12 entry.

Sample Name Sample Mass (mg) Pan / Lid Mass (mg)
NaMT 3.16 48.13
50% CEC NaMT w/ Bu3HdP+ 2.90 48.91
110% CEC NaMT w/ DMHXLBR 3.01 50.14
Laponite 3.06 50.18
110% CEC Laponite w/ DMHXLBR 3.08 49.52
90:10 PVOH 146K Laponite Dust 2.89 48.87
90:10 PVOH 146K Laponite Medium Clumps 2.96 48.89
90:10 PVOH 146K Laponite Large Clumps 3.07 48.18

Notes

  • After preparing the microspheres from the PVOH 146K Laponite, many of the spheres were not spherical. Large clumps of all sizes were produced rather than microspheres.
  • The microspheres prepared from PVOH 146K Laponite were rigid white crystalline structures with stacked layers.
  • Due to large sizes of the microspheres, they had to be ground up using a mortar and pestle before adding the 1μM rhodamine 6G dye solution.
  • Also DSC was taken of the different sizes of the microspheres to determine if the structure, function, and capability of the microspheres had changed due to extensive clumping.
  • When going through the process of preparing new microspheres from PVOH 146K 110% CEC Laponite w/ DMHXLBR, due to slowed vacuum filtration the sample was placed in a vial with the last solvent used for cleaning, methanol.
  • When freezing the new microsphere sample in liquid nitrogen, PVOH 146K 110% CEC Laponite w/ DMHXLBR, it was frozen in a medium of methanol and vacuum filtrated to remove the methanol residue.