*Clay 0.1118g | *Clay 0.1118g | ||
After the PVA with clay was mixed and cooled to room temperature 0.50 mL of glutaraldehyde was added. This mixture was then added drop wise to a burette that was filled with a solution of 20 mL %10 HCl and 60 mL of acetone (1:3 ratio) | After the PVA with clay was mixed and cooled to room temperature 0.50 mL of glutaraldehyde was added. This mixture was then added drop wise to a burette that was filled with a solution of 20 mL %10 HCl and 60 mL of acetone (1:3 ratio). | ||
It was observed that | |||
<!-- ##### DO NOT edit below this line unless you know what you are doing. ##### --> | <!-- ##### DO NOT edit below this line unless you know what you are doing. ##### --> | ||
Revision as of 10:46, 31 October 2014
 Project name
|
<html><img src="/images/9/94/Report.png" border="0" /></html> Main project page <html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>Previous entry<html> </html>Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html> |
Oct 29- PVA + Clay beads
ObjectiveAttempt to create beads using the PVA with clay and cross linking it with 10% HCl suspended in acetone. NotesPVA with clay was mixed using the procedure from Aug 27 Weights
After the PVA with clay was mixed and cooled to room temperature 0.50 mL of glutaraldehyde was added. This mixture was then added drop wise to a burette that was filled with a solution of 20 mL %10 HCl and 60 mL of acetone (1:3 ratio). It was observed that
| |