==Description==
==Description==
-
+
*masses of the hydrogels after the swelling study were measured.
-
==Data==
+
-
*Hydrogels (synthesized on http://openwetware.org/wiki/User:Samiye_Yaman/Notebook/Lab_581/2013/02/06) were sink at the bottom of the beaker. By using sonicator, the hydrogel were separated. Rest of solution was separated into layers by using seperatory funnel. Water was used.  
+
*Hydrogels (synthesized on http://openwetware.org/wiki/User:Samiye_Yaman/Notebook/Lab_581/2013/02/06) were sink at the bottom of the beaker. By using sonicator, the hydrogel were separated. After the vacuum filtration, observations under the microscope were made. The hydrogels were placed in to a lyophilizer for 24 hours.
 +
 
 +
*Rest of solution was separated into layers by using separatory funnel. Water was used.
 +
 
 +
==Data==
* Hydrogels placed in to various pH of HCl (http://openwetware.org/wiki/User:Samiye_Yaman/Notebook/Lab_581/2013/02/08) did not dissolve in any of the pHs.  
* Hydrogels placed in to various pH of HCl (http://openwetware.org/wiki/User:Samiye_Yaman/Notebook/Lab_581/2013/02/08) did not dissolve in any of the pHs.  
Line 24: Line 27:
1)Final mass of PVOH (MW: 146,000)=0.4526g
1)Final mass of PVOH (MW: 146,000)=0.4526g
 +
2)Final mass of PVOH (MW: 130,000)=0.8244g
2)Final mass of PVOH (MW: 130,000)=0.8244g
 +
3)Final mass of PVOH (MW: 89,000-98,000)=0.7608g
3)Final mass of PVOH (MW: 89,000-98,000)=0.7608g
 +
 +
*Photos from the microscope
 +
 +
[[Image:Hydrogel1.png|400px|]]
 +
 +
[[Image:Hydrogels2.png|400px|]]
 +
 +
[[Image:Hydrogels3.png|400px|]]
 +
 +
[[Image:Hydrogels4.png|400px|]]
 +
 +
[[Image:Hydrogels5.png|400px|]]
==Notes==
==Notes==

Current revision

Experimental Chemistry Main project page
Previous entry      Next entry



Contents

Objections

Description

  • masses of the hydrogels after the swelling study were measured.
  • Rest of solution was separated into layers by using separatory funnel. Water was used.

Data

1)Final mass of PVOH (MW: 146,000)=0.4526g

2)Final mass of PVOH (MW: 130,000)=0.8244g

3)Final mass of PVOH (MW: 89,000-98,000)=0.7608g

  • Photos from the microscope