User:Moira M. Esson/Notebook/CHEM-581/2013/04/03: Difference between revisions
(→DSC) |
|||
Line 87: | Line 87: | ||
'''Spectra''' | '''Spectra''' | ||
<br> | <br> | ||
Figure | Figure 7. Diffusion Testing of Rhodamine 6G in microspheres prepared with 90:10 ratio of PVA MW 146,000-186,000: 50% CEC NaMT | ||
<br> | <br> | ||
[[Image:90 pva 146 50NaMT micros diffusion.jpg]] | [[Image:90 pva 146 50NaMT micros diffusion.jpg]] | ||
Line 93: | Line 93: | ||
*Fluorescence intensity maximum is 6.985. | *Fluorescence intensity maximum is 6.985. | ||
<br> | <br> | ||
Figure | Figure 8. Diffusion Testing of Rhodamine 6G in microspheres prepared with 90:10 ratio of PVA MW 146,000-186,000: 110% Laponite | ||
<br> | <br> | ||
[[Image:90 PVA 146 110LP micros diff.jpg]] | [[Image:90 PVA 146 110LP micros diff.jpg]] | ||
Line 99: | Line 99: | ||
*Fluorescence intensity maximum is 5.109. | *Fluorescence intensity maximum is 5.109. | ||
<br> | <br> | ||
Figure | Figure 9. Diffusion Testing of Rhodamine 6G in microspheres prepared with a 90:10 ratio PVA 146,000-186,000: NaMT | ||
<br> | <br> | ||
[[Image:90 PVA 146 NaMT micros diff test.png]] | [[Image:90 PVA 146 NaMT micros diff test.png]] | ||
Line 105: | Line 105: | ||
*Fluorescence intensity maximum is 26.734 | *Fluorescence intensity maximum is 26.734 | ||
<br> | <br> | ||
Figure | Figure 10. Diffusion Testing of Rhodamine 6G in microspheres prepared with a 50:50 ratio PVA 146,000-186,000: NaMT | ||
<br> | <br> | ||
[[Image:50 PVA 146 NaMT micros diff.png]] | [[Image:50 PVA 146 NaMT micros diff.png]] | ||
*Fluorescence intensity maximum is 16.350 | *Fluorescence intensity maximum is 16.350 | ||
<br> | <br> | ||
Figure | Figure 11. Diffusion Testing of Rhodamine 6G in microspheres prepared with a 50:50 ratio PVA 146,000-186,000: 50% CEC NaMT | ||
<br> | <br> | ||
[[Image:50 PVA 146 50NaMT micros diff.png]] | [[Image:50 PVA 146 50NaMT micros diff.png]] | ||
Line 116: | Line 116: | ||
*Fluorescence intensity maximum is 11.661 | *Fluorescence intensity maximum is 11.661 | ||
<br> | <br> | ||
Figure | Figure 12. Diffusion Testing of Rhodamine 6G in microspheres prepared with a 50:50 ratio PVA 146,000-186,000: 110% CEC Laponite | ||
<br> | <br> | ||
[[Image:50 PVA 146 110 LP.png]] | [[Image:50 PVA 146 110 LP.png]] |
Revision as of 06:58, 15 April 2013
Project name | <html><img src="/images/9/94/Report.png" border="0" /></html> Main project page <html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>Previous entry<html> </html>Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html> | |||||||||||||||||||||
Objectives
DecantingThe general protocol described on 2013/03/01 was followed.
DSC
Diffusion TestingA new general protocol for the preparation of was used for the diffusion testing of the prepared microspheres. It was determined that the previous protocol did not allow for a quantitative understanding of the amount of dye diffused from the samples.
Notes
|