User:Moira M. Esson/Notebook/CHEM-581/2013/02/27

From OpenWetWare

(Difference between revisions)
Jump to: navigation, search
(Pressure tests)
(Pressure tests)
Line 15: Line 15:
*All pressure tests were conducted following the general protocol described on [[User:Moira_M._Esson/Notebook/CHEM-581/2013/02/22|2013/02/22]].
*All pressure tests were conducted following the general protocol described on [[User:Moira_M._Esson/Notebook/CHEM-581/2013/02/22|2013/02/22]].
<br>
<br>
-
Table
+
Table 1. Pressure testing information for hydrogels
 +
{| {{table}}
 +
| align="center" style="background:#f0f0f0;"|'''Sample Order'''
 +
| align="center" style="background:#f0f0f0;"|'''PVOH vs. Clay Ratio'''
 +
| align="center" style="background:#f0f0f0;"|'''PVOH Type'''
 +
| align="center" style="background:#f0f0f0;"|'''Clay Selection'''
 +
| align="center" style="background:#f0f0f0;"|'''Amount of Hydrogel Used (g)'''
 +
|-
 +
| 1||90:10||146K||110% CEC NaMT w/ DMHXLBR||0.1084
 +
|-
 +
| 2||90:10||130K||NaMT||0.1044
 +
|-
 +
| 3||50:50||146K||110% CEC NaMT||0.1092
 +
|-
 +
| 4||90:10||130K||110% CEC Laponite||0.1050
 +
|-
 +
| 5||50:50||130K||NaMT||0.1050
 +
|-
 +
| 6||90:10||130K||Laponite||0.1015
 +
|-
 +
| 7||50:50||146K||110% CEC Laponite||0.1080
 +
|-
 +
| 8||50:50||130K||Laponite||0.1036
 +
|-
 +
| 9||90:10||130K||110% CEC NaMT||0.1011
 +
|-
 +
| 10||50:50||130K||110% CEC Laponite||0.1036
 +
|-
 +
| 11||90:10||130K||110% CEC NaMT||0.1011
 +
|-
 +
| 12||90:10||146K||Laponite||0.1026
 +
|-
 +
| 13||50:50||130K||50% CEC NaMT Bu<sub>3</sub>HdP<sup>+</sup>||0.1052
 +
|-
 +
| 14||50:50||146K||Laponite||0.1045
 +
|-
 +
| 15||90:10||130K||50% CEC NaMT Bu<sub>3</sub>HdP<sup>+</sup>||0.1145
 +
|}
<br>
<br>
Figure 1. Image of bent pipette used for pressure testing
Figure 1. Image of bent pipette used for pressure testing

Revision as of 09:29, 7 March 2013

Project name Main project page
Previous entry      Next entry

Objectives

  1. Perform pressure tests on all prepared hydrogels using a bent pipette.
  2. Run fluorescence on the samples obtained from the pressure tests.


Pressure tests

  • Pressure tests were performed on all hydrogels prepared with Rhodamine 6G added.
  • After the sheer pressure test conducted on 2013/02/22, it was determined that a bent pipette and an unmodified pipette would be used to conduct the pressure tests. Each hydrogel will have at least two pressure tests conducted with the hydrogel: one with a bent pipette and the other with an unmodified pipette.
  • All pressure tests were conducted following the general protocol described on 2013/02/22.


Table 1. Pressure testing information for hydrogels

Sample Order PVOH vs. Clay Ratio PVOH Type Clay Selection Amount of Hydrogel Used (g)
190:10146K110% CEC NaMT w/ DMHXLBR0.1084
290:10130KNaMT0.1044
350:50146K110% CEC NaMT0.1092
490:10130K110% CEC Laponite0.1050
550:50130KNaMT0.1050
690:10130KLaponite0.1015
750:50146K110% CEC Laponite0.1080
850:50130KLaponite0.1036
990:10130K110% CEC NaMT0.1011
1050:50130K110% CEC Laponite0.1036
1190:10130K110% CEC NaMT0.1011
1290:10146KLaponite0.1026
1350:50130K50% CEC NaMT Bu3HdP+0.1052
1450:50146KLaponite0.1045
1590:10130K50% CEC NaMT Bu3HdP+0.1145


Figure 1. Image of bent pipette used for pressure testing Image:Bent pipette 2 27 13.jpg
Figure 2. Fluorescence of all NaMT hydrogel ssmples Figure 3. Fluorescence of all Lamponite hydrogel samples Figure 4. Fluorescence of all hydrogel samples