User:Moira M. Esson/Notebook/CHEM-581/2012/11/07 - Revision history

Moira M. Esson: /* FTIR */

2012-11-30T19:38:29Z

FTIR

←Older revision		Revision as of 19:38, 30 November 2012
Line 21:		Line 21:
	#PVOH(22K)+0.8wt% GA+100%CEC crosslinked spun 10 min CuSO4 prepared 10/26/2012		#PVOH(22K)+0.8wt% GA+100%CEC crosslinked spun 10 min CuSO4 prepared 10/26/2012
	#PVOH(22K)+0.8wt% GA+50% CEC crosslinked spun 10 min CuSO4 prepared 10/17/2012		#PVOH(22K)+0.8wt% GA+50% CEC crosslinked spun 10 min CuSO4 prepared 10/17/2012
		+	<br>
		+	[[Image:FTIR08GANaMT.jpg]]

	==UV-vis==		==UV-vis==

Moira M. Esson: /* UV-vis */

2012-11-11T03:08:49Z

UV-vis

←Older revision		Revision as of 03:08, 11 November 2012
Line 23:		Line 23:

	==UV-vis==		==UV-vis==
		+	*Prepared new porphyrin and sulfate salt solutions for UV-vis
		+	*In all preparations HPLC grade H<sub>2</sub>O was used
		+	*1.89μM porphyrine was added to 0.1mL, 0.2mL, 0.5mL or 1.0mL of salt
		+	*10mM Al<sub>2</sub>(SO<sub>4</sub>)<sub>3</sub>, 10mM Fe<sub>2</sub>(SO<sub>4</sub>)<sub>3</sub>, 10mM Na<sub>2</sub>SO<sub>4</sub> and 10mM of FeSO<sub>4</sub> was for the solutions
		+	* Four new solutions(using different amounts of the wanted salt) were prepared for each salt(either Al<sub>2</sub>(SO<sub>4</sub>)<sub>3</sub>, Fe<sub>2</sub>(SO<sub>4</sub>)<sub>3</sub>, Na<sub>2</sub>SO<sub>4</sub>, and FeSO<sub>4</sub>) making a total of 16 new solutions prepared.
		+	<br>
		+	Solution preparation:
		+	{\| {{table}}
		+	\| align="center" style="background:#f0f0f0;"\|'''Porphyrine'''
		+	\| align="center" style="background:#f0f0f0;"\|'''Al<sub>2</sub>(SO<sub>4</sub>)<sub>3</sub> concentration'''
		+	\| align="center" style="background:#f0f0f0;"\|'''Fe<sub>2</sub>(SO<sub>4</sub>)<sub>3</sub> concentration'''
		+	\| align="center" style="background:#f0f0f0;"\|'''FeSO<sub>4</sub> concentration'''
		+	\| align="center" style="background:#f0f0f0;"\|'''Na<sub>2</sub>SO<sub>4</sub> concentration'''
		+	\| align="center" style="background:#f0f0f0;"\|'''Volume of Water Added [mL]'''
		+	\|-
		+	\| 1.89 µM\|\|1 mM\|\|1 mM\|\|1 mM\|\|1 mM\|\|9.9
		+	\|-
		+	\| 1.89 µM\|\|2 mM\|\|2 mM\|\|2 mM\|\|2 mM\|\|9.8
		+	\|-
		+	\| 1.89 µM\|\|5 mM\|\|5 mM\|\|5 mM\|\|5 mM\|\|9.5
		+	\|-
		+	\| 1.89 µM\|\|10 mM\|\|10 mM\|\|10 mM\|\|10 mM\|\|9
		+	\|}
		+	<br>
		+	'''UV-Vis spectra''':
		+	<br>
	[[Image:Al2%28SO4%293.jpg]]		[[Image:Al2%28SO4%293.jpg]]
	<br><br>		<br><br>

Moira M. Esson: /* Objectives */

2012-11-11T02:59:02Z

Objectives

←Older revision		Revision as of 02:59, 11 November 2012
Line 7:		Line 7:
	<!-- ##### DO NOT edit above this line unless you know what you are doing. ##### -->		<!-- ##### DO NOT edit above this line unless you know what you are doing. ##### -->
	==Objectives==		==Objectives==
-	* ~~Insert content here~~...	+	# Finish running FTIR on remaining films.
		+	# Finish running UV-vis on porphyrin and sulfate salt solutions(must reprepare various concentrations)
		+	==FTIR==
		+	*The general protocol for FTIR was followed
		+	Films ran FTIR on:
		+	#PVOH(22K) 1.0067g+1mL GA+1mL porphyrin crosslinked
		+	#PVOH(22K)+0.5mL GA+0.104g NaMT crosslinked spun 10 min CuSO4 prepared 10/17/2012
		+	#PVOH(22K)+0.5mLGA+0.99mL porphyrin(no color on film )crosslinked prepared 10/19/2012
		+	#PVOH(22K)+1mL GA+100%CEC crosslinked prepared 10/4/2012
		+	#PVOH(22K)+1mL GA+1mL porphyrin crosslinked prepared 10/24/2012
		+	#PVOH(22K)+0.5mL GA+1mL porphyrin crosslinked prepared 10/24/2012 #2
		+	#PVOH(22K)+0.5mLGA+1mL porphyrin prepared crosslinked 10/26/2012
		+	#PVOH(22K)+0.8wt% GA+100%CEC crosslinked spun 10 min CuSO4 prepared 10/26/2012
		+	#PVOH(22K)+0.8wt% GA+50% CEC crosslinked spun 10 min CuSO4 prepared 10/17/2012
		+
	==UV-vis==		==UV-vis==
	[[Image:Al2%28SO4%293.jpg]]		[[Image:Al2%28SO4%293.jpg]]

Moira M. Esson: /* Entry title */

2012-11-11T01:40:52Z

Entry title

←Older revision		Revision as of 01:40, 11 November 2012
Line 6:		Line 6:
	\| colspan="2"\|		\| colspan="2"\|
	<!-- ##### DO NOT edit above this line unless you know what you are doing. ##### -->		<!-- ##### DO NOT edit above this line unless you know what you are doing. ##### -->
-	==~~Entry title~~==	+	==Objectives==
	* Insert content here...		* Insert content here...
		+	==UV-vis==
		+	[[Image:Al2%28SO4%293.jpg]]
		+	<br><br>
		+	[[Image:Fe2%28SO4%293.jpg]]
		+	<br><br>
		+	[[Image:FeSO4.jpg]]
		+	<br><br>
		+	[[Image:Na2SO4.jpg]]

Moira M. Esson: Autocreate 2012/11/07 Entry for User:Moira_M._Esson/Notebook/CHEM-581

2012-11-11T01:40:23Z

Autocreate 2012/11/07 Entry for User:Moira_M._Esson/Notebook/CHEM-581

New page

{|{{table}} width="800"
|-
|style="background-color: #EEE"|[[Image:owwnotebook_icon.png|128px]]<span style="font-size:22px;"> Project name</span>
|style="background-color: #F2F2F2" align="center"|<html><img src="/images/9/94/Report.png" border="0" /></html> [[{{#sub:{{FULLPAGENAME}}|0|-11}}|Main project page]]<br />{{#if:{{#lnpreventry:{{FULLPAGENAME}}}}|<html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>[[{{#lnpreventry:{{FULLPAGENAME}}}}{{!}}Previous entry]]<html>      </html>}}{{#if:{{#lnnextentry:{{FULLPAGENAME}}}}|[[{{#lnnextentry:{{FULLPAGENAME}}}}{{!}}Next entry]]<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html>}}
|-
| colspan="2"|

==Entry title==
* Insert content here...


|}

__NOTOC__