==Objectives==
==Objectives==
-
* Insert content here...
+
# Finish running FTIR on remaining films.
 +
# Finish running UV-vis on porphyrin and sulfate salt solutions(must reprepare various concentrations)
 +
==FTIR==
 +
*The general protocol for FTIR was followed
 +
Films ran FTIR on:
 +
#PVOH(22K) 1.0067g+1mL GA+1mL porphyrin crosslinked
 +
#PVOH(22K)+0.5mL GA+0.104g NaMT crosslinked spun 10 min CuSO4 prepared 10/17/2012
 +
#PVOH(22K)+0.5mLGA+0.99mL porphyrin(no color on film )crosslinked prepared 10/19/2012
 +
#PVOH(22K)+1mL GA+100%CEC crosslinked prepared 10/4/2012
 +
#PVOH(22K)+1mL GA+1mL porphyrin crosslinked prepared 10/24/2012
 +
#PVOH(22K)+0.5mL GA+1mL porphyrin crosslinked prepared 10/24/2012 #2
 +
#PVOH(22K)+0.5mLGA+1mL porphyrin prepared crosslinked 10/26/2012
 +
#PVOH(22K)+0.8wt% GA+100%CEC crosslinked spun 10 min CuSO4 prepared 10/26/2012
 +
#PVOH(22K)+0.8wt% GA+50% CEC crosslinked spun 10 min CuSO4 prepared 10/17/2012
 +
<br>
 +
[[Image:FTIR08GANaMT.jpg]]
 +
 
==UV-vis==
==UV-vis==
 +
*Prepared new porphyrin and sulfate salt solutions for UV-vis
 +
*In all preparations HPLC grade H<sub>2</sub>O was used
 +
*1.89μM porphyrine was added to 0.1mL, 0.2mL, 0.5mL or 1.0mL of salt
 +
*10mM Al<sub>2</sub>(SO<sub>4</sub>)<sub>3</sub>, 10mM Fe<sub>2</sub>(SO<sub>4</sub>)<sub>3</sub>, 10mM Na<sub>2</sub>SO<sub>4</sub> and 10mM of FeSO<sub>4</sub> was for the solutions
 +
* Four new solutions(using different amounts of the wanted salt) were prepared for each salt(either Al<sub>2</sub>(SO<sub>4</sub>)<sub>3</sub>, Fe<sub>2</sub>(SO<sub>4</sub>)<sub>3</sub>, Na<sub>2</sub>SO<sub>4</sub>, and FeSO<sub>4</sub>) making a total of 16 new solutions prepared.
 +
<br>
 +
Solution preparation:
 +
{| {{table}}
 +
| align="center" style="background:#f0f0f0;"|'''Porphyrine'''
 +
| align="center" style="background:#f0f0f0;"|'''Al<sub>2</sub>(SO<sub>4</sub>)<sub>3</sub> concentration'''
 +
| align="center" style="background:#f0f0f0;"|'''Fe<sub>2</sub>(SO<sub>4</sub>)<sub>3</sub> concentration'''
 +
| align="center" style="background:#f0f0f0;"|'''FeSO<sub>4</sub> concentration'''
 +
| align="center" style="background:#f0f0f0;"|'''Na<sub>2</sub>SO<sub>4</sub> concentration'''
 +
| align="center" style="background:#f0f0f0;"|'''Volume of Water Added [mL]'''
 +
|-
 +
| 1.89 µM||1 mM||1 mM||1 mM||1 mM||9.9
 +
|-
 +
| 1.89 µM||2 mM||2 mM||2 mM||2 mM||9.8
 +
|-
 +
| 1.89 µM||5 mM||5 mM||5 mM||5 mM||9.5
 +
|-
 +
| 1.89 µM||10 mM||10 mM||10 mM||10 mM||9
 +
|}
 +
<br>
 +
'''UV-Vis spectra''':
 +
<br>
[[Image:Al2%28SO4%293.jpg]]
[[Image:Al2%28SO4%293.jpg]]
<br><br>
<br><br>

Current revision

Project name Main project page
Previous entry      Next entry

Objectives

  1. Finish running FTIR on remaining films.
  2. Finish running UV-vis on porphyrin and sulfate salt solutions(must reprepare various concentrations)

FTIR

  • The general protocol for FTIR was followed

Films ran FTIR on:

  1. PVOH(22K) 1.0067g+1mL GA+1mL porphyrin crosslinked
  2. PVOH(22K)+0.5mL GA+0.104g NaMT crosslinked spun 10 min CuSO4 prepared 10/17/2012
  3. PVOH(22K)+0.5mLGA+0.99mL porphyrin(no color on film )crosslinked prepared 10/19/2012
  4. PVOH(22K)+1mL GA+100%CEC crosslinked prepared 10/4/2012
  5. PVOH(22K)+1mL GA+1mL porphyrin crosslinked prepared 10/24/2012
  6. PVOH(22K)+0.5mL GA+1mL porphyrin crosslinked prepared 10/24/2012 #2
  7. PVOH(22K)+0.5mLGA+1mL porphyrin prepared crosslinked 10/26/2012
  8. PVOH(22K)+0.8wt% GA+100%CEC crosslinked spun 10 min CuSO4 prepared 10/26/2012
  9. PVOH(22K)+0.8wt% GA+50% CEC crosslinked spun 10 min CuSO4 prepared 10/17/2012


Image:FTIR08GANaMT.jpg

UV-vis

  • Prepared new porphyrin and sulfate salt solutions for UV-vis
  • In all preparations HPLC grade H2O was used
  • 1.89μM porphyrine was added to 0.1mL, 0.2mL, 0.5mL or 1.0mL of salt
  • 10mM Al2(SO4)3, 10mM Fe2(SO4)3, 10mM Na2SO4 and 10mM of FeSO4 was for the solutions
  • Four new solutions(using different amounts of the wanted salt) were prepared for each salt(either Al2(SO4)3, Fe2(SO4)3, Na2SO4, and FeSO4) making a total of 16 new solutions prepared.


Solution preparation:

Porphyrine Al2(SO4)3 concentration Fe2(SO4)3 concentration FeSO4 concentration Na2SO4 concentration Volume of Water Added [mL]
1.89 µM1 mM1 mM1 mM1 mM9.9
1.89 µM2 mM2 mM2 mM2 mM9.8
1.89 µM5 mM5 mM5 mM5 mM9.5
1.89 µM10 mM10 mM10 mM10 mM9


UV-Vis spectra:
Image:Al2(SO4)3.jpg

Image:Fe2(SO4)3.jpg

Image:FeSO4.jpg

Image:Na2SO4.jpg