Data

←Older revision		Revision as of 16:04, 8 November 2012
Line 35:		Line 35:

	*PVOH MW 100,000- film was firmer and there was no apparent color change.		*PVOH MW 100,000- film was firmer and there was no apparent color change.
		+
	*PVOH MW 22000- no apparent color and physical change that was observed.		*PVOH MW 22000- no apparent color and physical change that was observed.
		+
	*PVOH MW 22000 cross linked with H3PO4- film became much tougher and turned a slight yellowish brown color.		*PVOH MW 22000 cross linked with H3PO4- film became much tougher and turned a slight yellowish brown color.
		+
	*PVOH MW 22000 with H3PO4 and maleic acid- no apparent color and physical change that was observed.		*PVOH MW 22000 with H3PO4 and maleic acid- no apparent color and physical change that was observed.
		+
	*PVOH MW 100,000 cross-linked w/ hydrochloric acid- slightly firm, but color change was very prominent- dark, jet blackish.		*PVOH MW 100,000 cross-linked w/ hydrochloric acid- slightly firm, but color change was very prominent- dark, jet blackish.

Mobeen Ashraf: /* Data */

Mobeen Ashraf — Thu, 08 Nov 2012 16:04:18 GMT

Data

←Older revision		Revision as of 16:04, 8 November 2012
Line 34:		Line 34:
	The films that were cross-linked in the oven had some considerable changes in color and toughness:		The films that were cross-linked in the oven had some considerable changes in color and toughness:

-	* PVOH MW 100,000- film was firmer and there was no apparent color change.	+	*PVOH MW 100,000- film was firmer and there was no apparent color change.
-	* PVOH MW 22000- no apparent color and physical change that was observed.	+	*PVOH MW 22000- no apparent color and physical change that was observed.
-	* PVOH MW 22000 cross linked with H3PO4- film became much tougher and turned a slight yellowish brown color.	+	*PVOH MW 22000 cross linked with H3PO4- film became much tougher and turned a slight yellowish brown color.
-	* PVOH MW 22000 with H3PO4 and maleic acid- no apparent color and physical change that was observed.	+	*PVOH MW 22000 with H3PO4 and maleic acid- no apparent color and physical change that was observed.
-	* PVOH MW 100,000 cross-linked w/ hydrochloric acid- slightly firm, but color change was very prominent- dark, jet blackish.	+	*PVOH MW 100,000 cross-linked w/ hydrochloric acid- slightly firm, but color change was very prominent- dark, jet blackish.

	==Notes==		==Notes==

Mobeen Ashraf: /* Data */

Mobeen Ashraf — Thu, 08 Nov 2012 16:03:35 GMT

Data

←Older revision		Revision as of 16:03, 8 November 2012
Line 31:		Line 31:
	==Data==		==Data==
	* Add data and results here...		* Add data and results here...
		+
		+	The films that were cross-linked in the oven had some considerable changes in color and toughness:
		+
		+	* PVOH MW 100,000- film was firmer and there was no apparent color change.
		+	* PVOH MW 22000- no apparent color and physical change that was observed.
		+	* PVOH MW 22000 cross linked with H3PO4- film became much tougher and turned a slight yellowish brown color.
		+	* PVOH MW 22000 with H3PO4 and maleic acid- no apparent color and physical change that was observed.
		+	* PVOH MW 100,000 cross-linked w/ hydrochloric acid- slightly firm, but color change was very prominent- dark, jet blackish.

	==Notes==		==Notes==

Mobeen Ashraf: /* Description */

Mobeen Ashraf — Thu, 08 Nov 2012 15:58:33 GMT

Description

←Older revision		Revision as of 15:58, 8 November 2012
Line 17:		Line 17:
	Following PVOH Films were Cross-linked:		Following PVOH Films were Cross-linked:

-	*1)PVOH film, MW of 22,000-placed in an oven set at 120 deg Celsius for 90 mins.	+	*1) PVOH film, MW of 22,000-placed in an oven set at 120 deg Celsius for 90 mins.
-	*2)PVOH film, MW of 100,000-placed in an oven set at 120 deg Celsius for 90 mins.	+	*2) PVOH film, MW of 100,000-placed in an oven set at 120 deg Celsius for 90 mins.
-	*3)PVOH film, MW of 100,000 cross-linked with HCl-placed in an oven set at 120 deg Celsius for 90 mins.	+	*3) PVOH film, MW of 100,000 cross-linked with HCl-placed in an oven set at 120 deg Celsius for 90 mins.
-	*4)PVOH film, MW of 22,000, cross-linked H3PO4-placed in an oven set at 120 deg Celsius for 90 mins.	+	*4) PVOH film, MW of 22,000, cross-linked H3PO4-placed in an oven set at 120 deg Celsius for 90 mins.
-	*5)PVOH film, MW of 22,000, cross-linked with maleic acid and H3PO4-placed in an oven set at 120 deg Celsius for 90 mins.	+	*5) PVOH film, MW of 22,000, cross-linked with maleic acid and H3PO4-placed in an oven set at 120 deg Celsius for 90 mins.

	'''DMA Analysis:'''		'''DMA Analysis:'''

Mobeen Ashraf: /* Description */

Mobeen Ashraf — Thu, 08 Nov 2012 15:58:12 GMT

Description

←Older revision		Revision as of 15:58, 8 November 2012
Line 26:		Line 26:

	PVOH films were subject to stretch( elastic tension ) mechanical analysis to test its mechanical durability.		PVOH films were subject to stretch( elastic tension ) mechanical analysis to test its mechanical durability.
		+
		+	* PVOH (film 1) was selected for DMA analysis. By using vernier calipers, the height and width of the film was measured to be 20.49 mm and 0.22 mm respectively.

	==Data==		==Data==

Mobeen Ashraf: /* Description */

Mobeen Ashraf — Thu, 08 Nov 2012 15:56:19 GMT

Description

←Older revision		Revision as of 15:56, 8 November 2012
Line 14:		Line 14:

	==Description==		==Description==
		+
		+	Following PVOH Films were Cross-linked:
		+
		+	*1)PVOH film, MW of 22,000-placed in an oven set at 120 deg Celsius for 90 mins.
		+	*2)PVOH film, MW of 100,000-placed in an oven set at 120 deg Celsius for 90 mins.
		+	*3)PVOH film, MW of 100,000 cross-linked with HCl-placed in an oven set at 120 deg Celsius for 90 mins.
		+	*4)PVOH film, MW of 22,000, cross-linked H3PO4-placed in an oven set at 120 deg Celsius for 90 mins.
		+	*5)PVOH film, MW of 22,000, cross-linked with maleic acid and H3PO4-placed in an oven set at 120 deg Celsius for 90 mins.
		+
		+	'''DMA Analysis:'''
		+
		+	PVOH films were subject to stretch( elastic tension ) mechanical analysis to test its mechanical durability.

	==Data==		==Data==

Mobeen Ashraf: /* Objective */

Mobeen Ashraf — Thu, 08 Nov 2012 15:45:24 GMT

Objective

←Older revision		Revision as of 15:45, 8 November 2012
Line 10:		Line 10:

	==Objective==		==Objective==
		+
		+	DMA- Dynamic Mechanical Analysis on PVOH films

	==Description==		==Description==

Mobeen Ashraf: Autocreate 2012/10/03 Entry for User:Mobeen_Ashraf/Notebook/Chem-581

Mobeen Ashraf — Thu, 08 Nov 2012 15:44:35 GMT

Autocreate 2012/10/03 Entry for User:Mobeen_Ashraf/Notebook/Chem-581

New page

{|{{table}} width="800"
|-
|style="background-color: #EEE"|[[Image:BDLlogo_notext_lr.png|128px]]<span style="font-size:22px;"> Experimental Chemistry</span>
|style="background-color: #F2F2F2" align="center"|<html><img src="/images/9/94/Report.png" border="0" /></html> [[{{#sub:{{FULLPAGENAME}}|0|-11}}|Main project page]]<br />{{#if:{{#lnpreventry:{{FULLPAGENAME}}}}|<html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>[[{{#lnpreventry:{{FULLPAGENAME}}}}{{!}}Previous entry]]<html>      </html>}}{{#if:{{#lnnextentry:{{FULLPAGENAME}}}}|[[{{#lnnextentry:{{FULLPAGENAME}}}}{{!}}Next entry]]<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html>}}
|-
| colspan="2"|


==Objective==

==Description==

==Data==
* Add data and results here...

==Notes==
This area is for any observations or conclusions that you would like to note.