User:Mobeen Ashraf/Notebook/Chem-581/2012/10/03: Difference between revisions
From OpenWetWare
Line 14: | Line 14: | ||
==Description== | ==Description== | ||
Following PVOH Films were Cross-linked: | |||
*1)PVOH film, MW of 22,000-placed in an oven set at 120 deg Celsius for 90 mins. | |||
*2)PVOH film, MW of 100,000-placed in an oven set at 120 deg Celsius for 90 mins. | |||
*3)PVOH film, MW of 100,000 cross-linked with HCl-placed in an oven set at 120 deg Celsius for 90 mins. | |||
*4)PVOH film, MW of 22,000, cross-linked H3PO4-placed in an oven set at 120 deg Celsius for 90 mins. | |||
*5)PVOH film, MW of 22,000, cross-linked with maleic acid and H3PO4-placed in an oven set at 120 deg Celsius for 90 mins. | |||
'''DMA Analysis:''' | |||
PVOH films were subject to stretch( elastic tension ) mechanical analysis to test its mechanical durability. | |||
==Data== | ==Data== |
Revision as of 08:56, 8 November 2012
Experimental Chemistry | <html><img src="/images/9/94/Report.png" border="0" /></html> Main project page <html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>Previous entry<html> </html>Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html> |
ObjectiveDMA- Dynamic Mechanical Analysis on PVOH films DescriptionFollowing PVOH Films were Cross-linked:
DMA Analysis: PVOH films were subject to stretch( elastic tension ) mechanical analysis to test its mechanical durability. Data
NotesThis area is for any observations or conclusions that you would like to note.
|