The films that were cross-linked in the oven had some considerable changes in color and toughness:
The films that were cross-linked in the oven had some considerable changes in color and toughness:
-
    * PVOH MW 100,000- film was firmer and there was no apparent color change.
+
*PVOH MW 100,000- film was firmer and there was no apparent color change.
-
    * PVOH MW 22000- no apparent color and physical change that was observed.
+
 
-
    * PVOH MW 22000 cross linked with H3PO4- film became much tougher and turned a slight yellowish brown color.
+
*PVOH MW 22000- no apparent color and physical change that was observed.
-
    * PVOH MW 22000 with H3PO4 and maleic acid- no apparent color and physical change that was observed.
+
 
-
    * PVOH MW 100,000 cross-linked w/ hydrochloric acid- slightly firm, but color change was very prominent- dark, jet blackish.
+
*PVOH MW 22000 cross linked with H3PO4- film became much tougher and turned a slight yellowish brown color.
 +
 
 +
*PVOH MW 22000 with H3PO4 and maleic acid- no apparent color and physical change that was observed.
 +
 
 +
*PVOH MW 100,000 cross-linked w/ hydrochloric acid- slightly firm, but color change was very prominent- dark, jet blackish.
==Notes==
==Notes==

Current revision

Experimental Chemistry Main project page
Previous entry      Next entry


Objective

DMA- Dynamic Mechanical Analysis on PVOH films

Description

Following PVOH Films were Cross-linked:

  • 1) PVOH film, MW of 22,000-placed in an oven set at 120 deg Celsius for 90 mins.
  • 2) PVOH film, MW of 100,000-placed in an oven set at 120 deg Celsius for 90 mins.
  • 3) PVOH film, MW of 100,000 cross-linked with HCl-placed in an oven set at 120 deg Celsius for 90 mins.
  • 4) PVOH film, MW of 22,000, cross-linked H3PO4-placed in an oven set at 120 deg Celsius for 90 mins.
  • 5) PVOH film, MW of 22,000, cross-linked with maleic acid and H3PO4-placed in an oven set at 120 deg Celsius for 90 mins.

DMA Analysis:

PVOH films were subject to stretch( elastic tension ) mechanical analysis to test its mechanical durability.

  • PVOH (film 1) was selected for DMA analysis. By using vernier calipers, the height and width of the film was measured to be 20.49 mm and 0.22 mm respectively.

Data

  • Add data and results here...

The films that were cross-linked in the oven had some considerable changes in color and toughness:

*PVOH MW 100,000- film was firmer and there was no apparent color change.
*PVOH MW 22000- no apparent color and physical change that was observed.
*PVOH MW 22000 cross linked with H3PO4- film became much tougher and turned a slight yellowish brown color.
*PVOH MW 22000 with H3PO4 and maleic acid- no apparent color and physical change that was observed.
*PVOH MW 100,000 cross-linked w/ hydrochloric acid- slightly firm, but color change was very prominent- dark, jet blackish.