User:Michael Corrado/Notebook/Experimental Chemistry Fall 2016/2016/09/21: Difference between revisions
From OpenWetWare
(fix raw html notebook nav) |
|||
(3 intermediate revisions by one other user not shown) | |||
Line 2: | Line 2: | ||
|- | |- | ||
|style="background-color: #EEE"|[[Image:owwnotebook_icon.png|128px]]<span style="font-size:22px;"> Project name</span> | |style="background-color: #EEE"|[[Image:owwnotebook_icon.png|128px]]<span style="font-size:22px;"> Project name</span> | ||
|style="background-color: #F2F2F2" align="center"| | |style="background-color: #F2F2F2" align="center"|[[File:Report.png|frameless|link={{#sub:{{FULLPAGENAME}}|0|-11}}]][[{{#sub:{{FULLPAGENAME}}|0|-11}}|Main project page]]<br />{{#if:{{#lnpreventry:{{FULLPAGENAME}}}}|[[File:Resultset_previous.png|frameless|link={{#lnpreventry:{{FULLPAGENAME}}}}]][[{{#lnpreventry:{{FULLPAGENAME}}}}{{!}}Previous entry]] }}{{#if:{{#lnnextentry:{{FULLPAGENAME}}}}|[[{{#lnnextentry:{{FULLPAGENAME}}}}{{!}}Next entry]][[File:Resultset_next.png|frameless|link={{#lnnextentry:{{FULLPAGENAME}}}}]]}} | ||
|- | |- | ||
| colspan="2"| | | colspan="2"| | ||
Line 15: | Line 15: | ||
#* The synthesis of 20% bentonite beads was prepared using the same procedure from [[User:Mary_Mendoza/Notebook/CHEM_581:_Experimental_Chemistry_I/2014/11/21| before]] with the only difference being the use of 16.66ml of 3% wt bentonite solution and 5.31ml of water. | #* The synthesis of 20% bentonite beads was prepared using the same procedure from [[User:Mary_Mendoza/Notebook/CHEM_581:_Experimental_Chemistry_I/2014/11/21| before]] with the only difference being the use of 16.66ml of 3% wt bentonite solution and 5.31ml of water. | ||
# Synthesis of 30% beads | # Synthesis of 30% beads | ||
#* The synthesis of the 30% beads was the same as that of the 20% beads with the only difference being the addition of 0.7498g of bentonite and 21.97 ml of DI water. | #* The synthesis of the 30% beads was the same as that of the 20% beads with the only difference being the addition of 0.7498g of bentonite powder and 21.97 ml of DI water. | ||
# Preparation of plastic columns | |||
#* The preparation of plastic columns for the 20% and 30% beads occurred using the same procedure detailed from [[User:Michael_Corrado/Notebook/Experimental_Chemistry_Fall_2016/2016/09/16| September 16th]]. | |||
# Film swelling | |||
#* ALl samples are tested by recording the mass of the patted-dry films, placing them in the oven for 2 hours at 100°C, then recording the mass of the dry films: | |||
#* Two pieces of the 0.5ml glutaraldehyde and PVOH film were tested. | |||
#* Three pieces of the 1.0ml glutaraldehyde and PVOH film were tested. | |||
Latest revision as of 02:02, 27 September 2017
Project name | Main project page Previous entry Next entry |
Objectives
Procedure
|