Objectives

  • Grind 100Ag-LMT made on 2013/02/05 into a fine powder.
  • Make PLA2002D + 5 wt% 100Ag-LMT film.
  • Make PLA2002D + 5 wt% LMT film.

PLA2002D Films

  • The protocol on 2013/02/06 was used to make the films.
  • Each film contained 5 wt% of 100Ag-LMT or LMT for one gram of PLA2002D.


  • PLA2002D + 5 wt% LMT film
    • Theoretical mass PLA2002D: 1 g
    • Theoretical mass LMT: 0.05 g
    • Actual mass PLA2002D: 1.009185 g
    • Actual mass LMT: 0.05060 g


  • PLA2002D + 5 wt% 100Ag-LMT film
    • Theoretical mass PLA2002D: 1 g
    • Theoretical mass 100Ag-LMT: 0.05 g
    • Actual mass PLA2002D: 1.01686 g
    • Actual mass 100Ag-LMT: 0.05062 g
    • Final mass of PLA2002D + 5 wt% 100Ag-LMT: 0.97 g


  • Actual content of silver in 0.5 g PLA2002D + 5 wt% 100Ag-LMT:


  0.00622 g AgNO3 × (1 mol AgNO3/169.87 g AgNO3) × (1 mol Ag+/1 mol AgNO3) = 3.66 × 10-5 mol Ag+
  [Ag+] in 5 mL 100Ag-LMT filtrate was 0.000253614 M
  0.000253614 M Ag+ × 0.005 L = 1.2681 × 10-6 mol Ag+
  Therefore, 3.66 × 10-5 mol Ag+ − 1.2681 × 10-6 mol Ag+ = 3.53 × 10-5 mol Ag+ was exchanged into 100Ag-LMT.


  0.05 × 0.5 g PLA2002D + 5 wt% 100Ag-LMT = 0.025 g 100Ag-LMT
  (3.53 × 10-5 mol Ag+) ÷ (0.05062 g 100Ag-LMT) = x mol Ag+ ÷ (0.025 g 100Ag-LMT)
  4.47 × 10-8mol Ag+ in 0.025 g 100Ag-LMT of 0.5 g PLA2002D + 5 wt% 100Ag-LMT film