User:Melissa Novy/Notebook/CHEM-571/2012/11/28

From OpenWetWare

(Difference between revisions)
Jump to: navigation, search
(Objectives)
Line 19: Line 19:
* Resuspend AuADA fibers in solutions made on [[User:Melissa_Novy/Notebook/CHEM-571/2012/11/27|2012/11/27]] with Tris buffer.
* Resuspend AuADA fibers in solutions made on [[User:Melissa_Novy/Notebook/CHEM-571/2012/11/27|2012/11/27]] with Tris buffer.
 +
==UV-Vis Analysis of AuADA Solutions==
 +
* The spectra of AuADA solutions were collected over 200 nm to 800 nm.
 +
[[Image:AuADA_11272012.png]]
 +
* A peak at around 520 nm was visible in the spectra of the following mole ratio Au:ADA solutions: 60 through 130.  This peak is likely due to the presence of GNPs in these solutions.
<!-- ##### DO NOT edit below this line unless you know what you are doing. ##### -->
<!-- ##### DO NOT edit below this line unless you know what you are doing. ##### -->

Revision as of 19:47, 29 November 2012

Search this Project

Customize your entry pages

Objectives

  • Analyze AuADA solutions made on 2012/11/27 with UV-vis and AA spectroscopy.
  • Resuspend AuADA fibers in solutions made on 2012/11/27 with Tris buffer.

UV-Vis Analysis of AuADA Solutions

  • The spectra of AuADA solutions were collected over 200 nm to 800 nm.

Image:AuADA_11272012.png

  • A peak at around 520 nm was visible in the spectra of the following mole ratio Au:ADA solutions: 60 through 130. This peak is likely due to the presence of GNPs in these solutions.