====Film Masses for Density Calculations==== | ====Film Masses for Density Calculations==== | ||
{| {{table}} | {| {{table}} | ||
| align="center" style="background:#f0f0f0;"|''' | | align="center" style="background:#f0f0f0;"|'''Film''' | ||
| align="center" style="background:#f0f0f0;"|'''Initial Mass''' | |||
| align="center" style="background:#f0f0f0;"|'''Mass | | align="center" style="background:#f0f0f0;"|'''Dried Mass''' | ||
| align="center" style="background:#f0f0f0;"|'''Mass | | align="center" style="background:#f0f0f0;"|'''Displaced Volume''' | ||
| align="center" style="background:#f0f0f0;"|''' | |||
|- | |- | ||
| || | | PVA film|| 0.0278g || 0.0102g || 0.048mL | ||
|- | |- | ||
| || | | || 0.0255g || 0.0129g || | ||
|- | |- | ||
| || | | || 0.0265g || 0.0089g || 0.114mL | ||
|- | |- | ||
| || | | PVA-Clay film|| 0.0122g || 0.0067g || | ||
|- | |- | ||
| || | | || 0.0177g ||0.0102g || | ||
|- | |- | ||
| || | | || 0.0307g || 0.0145g || | ||
|} | |} | ||
====BPA Sample Prep==== | ====BPA Sample Prep==== | ||
Line 71: | Line 46: | ||
| align="center" style="background:#f0f0f0;"|'''Sample''' | | align="center" style="background:#f0f0f0;"|'''Sample''' | ||
| align="center" style="background:#f0f0f0;"|'''Vial''' | | align="center" style="background:#f0f0f0;"|'''Vial''' | ||
| align="center" style="background:#f0f0f0;"|'''Mass of Empty Vial''' | | align="center" style="background:#f0f0f0;"|'''Mass of Empty Vial (g)''' | ||
| align="center" style="background:#f0f0f0;"|'''Mass of Film + Vial''' | | align="center" style="background:#f0f0f0;"|'''Mass of Film + Vial (g)''' | ||
| align="center" style="background:#f0f0f0;"|'''Film Mass''' | | align="center" style="background:#f0f0f0;"|'''Film Mass (g)''' | ||
|- | |- | ||
| GC-MS || 10/22 5 min|| 13.0961 | | GC-MS || 10/22 5 min|| 13.0961 || 13.2417 || 0.1456 | ||
|- | |- | ||
| || 10/22 15 min || 13.0637 | | || 10/22 15 min || 13.0637 || 13.1933 || 0.1296 | ||
|- | |- | ||
| || 10/22 30 min || 13.0670 | | || 10/22 30 min || 13.0670 || 13.2869 || 0.2199 | ||
|- | |- | ||
| || 10/22 60 min|| 13.0693 | | || 10/22 60 min|| 13.0693 || 13.2071 || 0.1378 | ||
|- | |- | ||
| || 10/22 120 min || 13.0977 | | || 10/22 120 min || 13.0977 || 13.3447 || 0.2470 | ||
|- | |- | ||
| || 10/22 afternoon || 13.0519 | | || 10/22 afternoon || 13.0519 || 13.2186 || 0.1667 | ||
|- | |- | ||
| || 10/23 morning || 13.0361 | | || 10/23 morning || 13.0361 || 13.1181 || 0.0820 | ||
|- | |- | ||
| || 10/23 afternoon || 13.0016 | | || 10/23 afternoon || 13.0016 || 13.1543 || 0.1527 | ||
|- | |- | ||
| || 10/24 || 13.0731 | | || 10/24 || 13.0731 || 13.2344 || 0.1613 | ||
|- | |- | ||
| HPLC || 10/22 5 min|| 13.0393 | | HPLC || 10/22 5 min|| 13.0393 || 13.2924 || 0.2531 | ||
|- | |- | ||
| || 10/22 15 min || 13.0428 | | || 10/22 15 min || 13.0428 || 13.1814 || 0.1386 | ||
|- | |- | ||
| || 10/22 30 min || 13.0879 | | || 10/22 30 min || 13.0879 || 13.3509 || 0.2630 | ||
|- | |- | ||
| || 10/22 60 min|| 13.1562 | | || 10/22 60 min|| 13.1562 || 13.3389 || 0.1827 | ||
|- | |- | ||
| || 10/22 120 min || 13.1078 | | || 10/22 120 min || 13.1078 || 13.2840 || 0.1762 | ||
|- | |- | ||
| || 10/22 afternoon || 13.0813 | | || 10/22 afternoon || 13.0813 || 13.1784 || 0.0971 | ||
|- | |- | ||
| || 10/23 morning || 13.1008 | | || 10/23 morning || 13.1008 || 13.2877 || 0.1869 | ||
|- | |- | ||
| || 10/23 afternoon || 13.0785 | | || 10/23 afternoon || 13.0785 || 13.2066 || 0.1281 | ||
|- | |- | ||
| || 10/24 || 13.0254 | | || 10/24 || 13.0254 || 13.1791 || 0.1537 | ||
|} | |} | ||
Revision as of 08:18, 22 October 2014
CHEM 581: Experimental Chemistry | <html><img src="/images/9/94/Report.png" border="0" /></html> Main project page <html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>Previous entry<html> </html>Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html> | |||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
October 22, 2014ProceduresFinish Film Synthesis from 10/17Film Masses for Density Calculations
BPA Sample Prep
Data |