Klare Lazor (talk | contribs) |
||
Line 72: | Line 72: | ||
1) | 1) | ||
a) | a)PVOH=0.5 grams + 5ml of water dissolved on hot plate + 1ml of glutaraldehyde | ||
**clear and rather thick compared to without glutaraldehyde | **clear and rather thick compared to without glutaraldehyde | ||
b) | b)PVOH~.4 grams + 5ml of water dissolved on hot plate with .1262 g PDMS + glutaraldehyde | ||
** clear and rather thick compared to without glutraraldehyde | ** clear and rather thick compared to without glutraraldehyde | ||
Line 90: | Line 88: | ||
3) | 3) | ||
a) | a)Prepare 1.0g PVOH ~ 1.0058g with .1g Na-MT~.1069g heat to dissolve and get a homogeneous mixture + 1ml of glutaraldehyde | ||
b) | b)Prepare 1.0g PVOH with .1g 100% CEC Surfactant Clayto dissolve and get a homogeneous mixture + 1ml of glutaraldehyde | ||
==Notes== | ==Notes== |
Revision as of 09:39, 1 October 2012
Biomaterials Design Lab | <html><img src="/images/9/94/Report.png" border="0" /></html> Main project page <html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>Previous entry<html> </html>Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html> |
Objective1) remade glutaraldehyde films with pdms and glutaraldehyde
Descriptionwith glutaraldehyde make sure to wear completely covered goggles on face when handeling
a)
b)
2) Na-MT~.1grams (repeating with 50% and 100% CEC surfactant clay) added to 20ml CuSO4*5H20 underfume hood
3) a)
b)
Data/observations1) a)PVOH=0.5 grams + 5ml of water dissolved on hot plate + 1ml of glutaraldehyde
b)PVOH~.4 grams + 5ml of water dissolved on hot plate with .1262 g PDMS + glutaraldehyde
2) Na-MT~.1grams (repeating with 50% and 100% CEC surfactant clay) added to 20ml CuSO4*5H20 underfume hood
3) a)Prepare 1.0g PVOH ~ 1.0058g with .1g Na-MT~.1069g heat to dissolve and get a homogeneous mixture + 1ml of glutaraldehyde
NotesThis area is for any observations or conclusions that you would like to note.
|