- ADA protein were transferred from dialysis tubing into 15mL falcon tubes
- Make Au/ADA samples with the following mole ratios: 60 - 70 - 80 - 90 - 100 - 110 - 120 - 130 - 140 - 150, with ADA fraction 2 after dialysis.
- Un-dialyzed Au/ADA samples and Au/HRP made on 2012/11/14 were run on UV-vis spectrometer and Atomic Absorption Spectrometer in order to compare spectra results for Au/ADA, Au/HRP, Au/Lysozyme, and Au/BSA.
- Resuspend Au/HRP samples in different concentration and pH of Tris buffer to test ionic strength.
Procedure for Dialysis
- Dialysis beaker containing dialysis tubing enclosed with ADA protein fractions were taken from the 4°C cold room into room temperature lab room.
- The dialysis clips were taken off from dialysis tubing. ADA protein fractions were poured into a sterile 15mL falcon tubes.
- This process was repeated for all three protein fractions: ADA fraction 1&3 made on 2012/11/06, ADA fraction 2 made on 2012/11/06, and ADA fraction purified on 2012/10/03.
- ADA fractions in 15mL falcon tubes were stored in 4°C refrigerator.
Notes for Dialysis
- It was observed that white precipitants were found at the bottom of dialysis tubing, and suspected that due to a lack of salt in solution with ADA proteins, the ADA proteins falls out of solution. This could predict a potential difference in UV-vis and Atomic Absorption spectrometer results in finalized product of Au/ADA samples made with dialyzed ADA compare to Au/ADA samples made on 2012/11/14.
Procedure for making dialyzed Au/ADA samples
- Au/ADA samples were made with the following mole ratios:
60 - 70 - 80 - 90 - 100 - 110 - 120 - 130 - 140 - 150
- Stock solution of HAuCl4 was made on 2012/09/05 with a concentration of 10.5uM.
- Stock solution for ADA was the ADA protein fraction made in 2012/10/03 after dialysis. The ADA stock solution has a concentration of 58.36μM.
- Volume of ADA protein was set at 137.1uL and a range of HAuCl4 was used from 45.71μL to 114.3μL. Water was added to the sample to increase the volume of sample to 8mL. Volumes of each reactants are shown in table below:
||HAuCl4 Added [uL]
- The samples were made in 15mL non-sterile falcon tubes. After all reactants were added, samples are capped and wrapped around with aluminum foil.
- Samples were placed in incubator at 85°C for 4 hours then cooled down to room temperature.
Procedure for Running UV-vis Spectrometer on Au/ADA and Au/HRP samples
- UV-vis spectrometer were run in spectrum method. A range of 200nm to 800nm were ran on all Au/ADA and Au/HRP samples both made on 2012/11/14.
- 3mL of distilled water was placed in quartz cuvette with 1cm pathlength and set as base line solution. 3mL taken from supernatant of Au/ADA and Au/HRP samples were placed in an identical quartz cuvette with 1cm pathlength for spectra measurement.
- After measurement, each 3mL samples of Au/ADA and Au/HRP of different mole ratios were placed back into original sample test tubes to conserve products that would later be used for Atomic Absorption spectra analysis.
Results for Running UV-vis Spectrometer on Au/ADA and Au/HRP samples
- Au/ADA samples appeared clear, and no purple fibers were formed. This also indicates that no gold nanoparticles were present in solution. However, there were white precipitants observed at the bottom of the samples in samples with molar ratio 130 to 150. The white precipitants appear in small circular quantities and seemed to stick to the side of the glass test tube. A picture of white precipitant in Au/ADA with 150 mole ratio is shown below:
- It was suspected that the white precipitant could be precipitated ADA proteins when gold interacts with the salt in elution buffer. The elution buffer contained the following contents: 20mM Tris, 0.5M NaCl, and 500mM Imidazole at pH 7.5. Once salt is attracted to interact with HAuCl4 in solution, ADA protein then precipitates due to lack of buffering for stabilization.
- Au/HRP samples appeared purple in color. All samples had purple supernatant. Small fibers were observed for sample with mole ratio 130 to 150. For samples with 100 to 150 molar ratio, supernatant displayed a darker purple color compare to samples with 60 to 90 molar ratio.
- UV-vis spectrometer were run for Au/ADA samples. Absorbance versus wavelength ranging from 200nm to 800nm were plotted on the graph titled "Absorbance of AuADA Solutions at Mole Ratios from 60 to 140 Au:ADA", shown below:
- From graph above, it can be shown that Au/ADA samples have very low absorbance. This indicates that litle to none gold nanoparticles were formed within solution. It was also suspected a potential peak around 700nm from seeing the overall trend for all samples. However, that peak would most likely be due to the salt present in elution buffer.
- UV-vis spectrometer were run for Au/HRP samples. Absorbance were graphed versus wavelength for samples with mole ratio ranging from 60 to 150. The graph titled "Absorbance of Solutions of AuHRP at Mole Ratios from 60 to 150 Au:HRP" is shown below:
- From the graph, it can be suggested that 150 Au/HRP solution yielded the most amount of absorbance. This result seemed consistent to the procedure for making Au/HRP solutions since most amount of HAuCl4 was placed into the 150 Au/HRP sample.
- The results from UV-vis spectra also suggested gold nanoparticles were present in all solutions. Maximum concentrations of gold nanoparticles were present in 150 Au/HRP samples while 60 Au/HRP sample contained the least concentrations of gold nanoparticles.