User:Karlena L. Brown/Notebook/PVOH Research/2013/03/22: Difference between revisions

From OpenWetWare
Jump to navigationJump to search
Line 25: Line 25:
| align="center" style="background:#f0f0f0;"|'''PVOH 146K Mass (g)'''
| align="center" style="background:#f0f0f0;"|'''PVOH 146K Mass (g)'''
| align="center" style="background:#f0f0f0;"|'''Actual Clay Mass (g)'''
| align="center" style="background:#f0f0f0;"|'''Actual Clay Mass (g)'''
| align="center" style="background:#f0f0f0;"|'''H<sub>2</sub>O Added (mL)'''
| align="center" style="background:#f0f0f0;"|'''H<sub>2</sub>O Added (mL)'''
| align="center" style="background:#f0f0f0;"|'''H<sub>2</sub>O Added (mL)'''
|-
|-
| 50:50||NaMT||0.02530||0.02530||40
| 50:50||NaMT||0.02530||0.02530||20||35
|-
|-
| 50:50||Laponite||0.02590||0.02500||40
| 50:50||Laponite||0.02590||0.02500||20||35
|-
|-
| 90:10||NaMT||0.04140||0.01110||40
| 90:10||NaMT||0.04140||0.01110||20||35
|-
|-
| 90:10||Laponite||0.04470||0.01100||40
| 90:10||Laponite||0.04470||0.01100||20||35
|-
|-
| 50:50||110% CEC Laponite w/ DMHXLBR||0.02550||0.02500||40
| 50:50||110% CEC Laponite w/ DMHXLBR||0.02550||0.02500||20||35
|-
|-
| 90:10||110% CEC Laponite w/ DMHXLBR||0.04230||0.01150||40
| 90:10||110% CEC Laponite w/ DMHXLBR||0.04230||0.01150||20||35
|-
|-
| 50:50||50% CEC NaMT w/ Bu<sub>3</sub>HdP<sup>+</sup>||0.02540||0.02500||40
| 50:50||50% CEC NaMT w/ Bu<sub>3</sub>HdP<sup>+</sup>||0.02540||0.02500||20||35
|-
|-
| 90:10||50% CEC NaMT w/ Bu<sub>3</sub>HdP<sup>+</sup>||0.04010||0.01050||40
| 90:10||50% CEC NaMT w/ Bu<sub>3</sub>HdP<sup>+</sup>||0.04010||0.01050||20||35
|}
|}


Revision as of 18:45, 8 April 2013

PVOH Research <html><img src="/images/9/94/Report.png" border="0" /></html> Main project page
<html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>Previous entry<html>&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;</html>Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html>

OBJECTIVES

  • Prepare more microsphere samples expanding upon new previous method developed (new modifications)

PVOH 130K Prepared Microsphere Samples & Dye Preparations 2

RECALL MICROSPHERE PREPARATION PROTOCOL ON 2/20/13

1μM Rhodamine 6G Dye Concentration (90:10) 

  M1V1 = M2V2
  1μM (RG6)x 10mL = (92μM)V2    V2 = 109μL

1μM Rhodamine 6G Dye Concentration (50:50) 

  M1V1 = M2V2
  1μM (RG6)x 10mL = (165μM)V2    V2 = 61μL
PVOH vs. Clay Ratio Clay Selection PVOH 146K Mass (g) Actual Clay Mass (g) H2O Added (mL) H2O Added (mL)
50:50 NaMT 0.02530 0.02530 20 35
50:50 Laponite 0.02590 0.02500 20 35
90:10 NaMT 0.04140 0.01110 20 35
90:10 Laponite 0.04470 0.01100 20 35
50:50 110% CEC Laponite w/ DMHXLBR 0.02550 0.02500 20 35
90:10 110% CEC Laponite w/ DMHXLBR 0.04230 0.01150 20 35
50:50 50% CEC NaMT w/ Bu3HdP+ 0.02540 0.02500 20 35
90:10 50% CEC NaMT w/ Bu3HdP+ 0.04010 0.01050 20 35

Notes

  • Originally, samples were being prepared on a 0.1 gram scale; however, since then samples were divided into 1/4. New modifications include:
  # 50:50 clay vs. PVOH samples, the max amount being used is 0.025 grams for each substance
  # 90:10 clay vs. PVOH samples, the max amount being used is 0.01 grams clay and 0.04 grams PVOH
  • Based upon new sample modifications using 1/4 the original ratio, microsphere samples have began to form actual smaller microspheres rather than microgels or connected large clumps of spheres
Retrieved from "https://openwetware.org/mediawiki/index.php?title=User:Karlena_L._Brown/Notebook/PVOH_Research/2013/03/22&oldid=689852"