User:Karlena L. Brown/Notebook/PVOH Research/2013/02/27

From OpenWetWare

(Difference between revisions)
Jump to: navigation, search
(→PVOH Film Preparations)
(→Hydrogel Pressure Samples Tested)
Line 8: Line 8:
==OBJECTIVES==
==OBJECTIVES==
==Hydrogel Pressure Samples Tested==
==Hydrogel Pressure Samples Tested==
 +
'''RECALL HYDROGEL PRESSURE TESTING PROTOCOL ON 2/20/13 & FLUORESCENCE ANALYSIS PROCEDURES ON 2/13/13'''
 +
 +
{| {{table}}
 +
| align="center" style="background:#f0f0f0;"|'''Sample Order'''
 +
| align="center" style="background:#f0f0f0;"|'''PVOH vs. Clay Ratio'''
 +
| align="center" style="background:#f0f0f0;"|'''PVOH Type'''
 +
| align="center" style="background:#f0f0f0;"|'''Clay Selection'''
 +
| align="center" style="background:#f0f0f0;"|'''Amount of Hydrogel Used (g)'''
 +
|-
 +
| 1||90:10||146K||110% CEC NaMT w/ DMHXLBR||0.1084
 +
|-
 +
| 2||90:10||130K||NaMT||0.1044
 +
|-
 +
| 3||50:50||146K||110% CEC NaMT w/ DMHXLBR||0.1092
 +
|-
 +
| 4||90:10||130K||110% CEC Laponite w/ DMHXLBR||0.1050
 +
|-
 +
| 5||50:50||130K||NaMT||0.1050
 +
|-
 +
| 6||90:10||130K||Laponite||0.1015
 +
|-
 +
| 7||50:50||146K||110% CEC Laponite w/ DMHXLBR||0.1080
 +
|-
 +
| 8||50:50||130K||Laponite||0.1036
 +
|-
 +
| 9||90:10||130K||110% CEC NaMT w/ DMHXLBR||0.1011
 +
|-
 +
| 10||50:50||130K||110% CEC Laponite w/ DMHXLBR||0.1036
 +
|-
 +
| 11||90:10||130K||110% CEC NaMT w/ DMHXLBR||0.1011
 +
|-
 +
| 12||90:10||146K||Laponite||0.1026
 +
|-
 +
| 13||50:50||130K||50% CEC NaMT w/ Bu<sub>3</sub>HdP<sup>+</sup>||0.1052
 +
|-
 +
| 14||50:50||146K||Laponite||0.1045
 +
|-
 +
| 15||90:10||130K||50% CEC NaMT w/ Bu<sub>3</sub>HdP<sup>+</sup>||0.1145
 +
|}
 +
==Notes==
==Notes==
* The pipettes that provided the best fluorescence results for each sample were both the straight plastic pipette and 90° angle bent pipette.
* The pipettes that provided the best fluorescence results for each sample were both the straight plastic pipette and 90° angle bent pipette.

Revision as of 23:55, 4 March 2013

PVOH Research Main project page
Previous entry      Next entry

OBJECTIVES

Hydrogel Pressure Samples Tested

RECALL HYDROGEL PRESSURE TESTING PROTOCOL ON 2/20/13 & FLUORESCENCE ANALYSIS PROCEDURES ON 2/13/13

Sample Order PVOH vs. Clay Ratio PVOH Type Clay Selection Amount of Hydrogel Used (g)
190:10146K110% CEC NaMT w/ DMHXLBR0.1084
290:10130KNaMT0.1044
350:50146K110% CEC NaMT w/ DMHXLBR0.1092
490:10130K110% CEC Laponite w/ DMHXLBR0.1050
550:50130KNaMT0.1050
690:10130KLaponite0.1015
750:50146K110% CEC Laponite w/ DMHXLBR0.1080
850:50130KLaponite0.1036
990:10130K110% CEC NaMT w/ DMHXLBR0.1011
1050:50130K110% CEC Laponite w/ DMHXLBR0.1036
1190:10130K110% CEC NaMT w/ DMHXLBR0.1011
1290:10146KLaponite0.1026
1350:50130K50% CEC NaMT w/ Bu3HdP+0.1052
1450:50146KLaponite0.1045
1590:10130K50% CEC NaMT w/ Bu3HdP+0.1145

Notes

  • The pipettes that provided the best fluorescence results for each sample were both the straight plastic pipette and 90° angle bent pipette.
  • All samples run maintained a composition incorporating Rhodamine 6G dye
  • All samples on 2/27/13 were tested using the bent pipette containing the 90° angle. (See figure listed below)

Figure 1. Image of bent pipette used for pressure testing Image:Bent pipette 2 27 13.jpg