==Objective== | |||
# UV-vis and fluorescence of all 6 QD synthesis from 04/02/14. | |||
# Make BSA solution 0.1459mM | |||
# De-gas all solutions | |||
# Synthesis using Gonzalez Method | |||
# Continue precipitation of 78% BSA by mass (second trial) | |||
*BSA made using 0.2409g in 25mL --> 0.1459mM BSA | |||
==Protocol== | |||
This protocol was taken from [[User:Matt Hartings/Notebook/AU Biomaterials Design Lab/2014/02/03|Matt Harting's]] notebook, all solutions de-gassed before synthesis. | |||
# To a 3-necked flask is added | |||
# | ## 25mL of 20 mM L-cysteine (roughly 22% L-Cysteine) | ||
## 25mL .1459 mM BSA (roughly 78% by mass) | |||
## 5mL of 100mM ZnSO<sub>4</sub> (0.5 mmol) | |||
## 5.437mL of 10.3mM MnCl<sub>2</sub> (0.056 mmol) | |||
## The pH of this mixture is adjusted to 11 with ~1M NaOH (should be on the order of 60uL) | |||
# This mixture is stirred under Ar (I'll use N<sub>2</sub>) for 30 minutes | |||
# 5.505mL of 101mM Na<sub>2</sub>S is quickly added. | |||
# The solution is stirred for 20 minutes | |||
# The solution is then aged at 50C under air for 2 hours. | |||
==Notes== | ==Notes== | ||
*All solutions were degassed for approximately 10-15 minutes depending on the total volume of the solution | |||
Revision as of 22:56, 20 April 2014
Biomaterials Design Lab | <html><img src="/images/9/94/Report.png" border="0" /></html> Main project page <html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>Previous entry<html> </html>Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html> |
Objective
ProtocolThis protocol was taken from Matt Harting's notebook, all solutions de-gassed before synthesis.
Notes
|