==Objective== | ==Objective== | ||
To crosslink the films prepared last class, to test the effects of using a lower molecular weight PVOH on the film, and to prepare a 0.2 M NaOH solution for use next class. | |||
==Description== | ==Description== | ||
<u>Crosslinking</u> | |||
# Determined the concentration of HCl needed, by determining the concentration of H<sub>2</sub>SO<sub>4</sub> | |||
<u>Preparation of Lower Weight PVOH Films</u> | |||
# Measured out 6 1 g samples of PVOH (MW = 22,000) | |||
# Prepared a solution of 0.22 g phenol in 10 mL water. | |||
# Dissolved the PVOH samples in 30 mL water (in 100 mL beakers) | |||
# Once the PVOH had dissolved, the corresponding amounts of phenol solution were added (1% film = 1 mL, 0.1% = | |||
<u>NaOH Calculations and Preparation</u> | |||
* need to prepare 50 mL of a 0.2 NaOH solution from a 0.5 N NaOH soln. | |||
(0.5 moles/L)(X) = (0.2 moles/L)(0.05 L) → X = 0.02 L = 20 mL | |||
# Measure out 20 mL 0.50 NaOH | |||
# Add to 30 mL water | |||
# Save for use on Friday. | |||
==Data== | ==Data== | ||
No data was collected today. | |||
==Notes== | ==Notes== | ||
<u> Description of Films Prepared Last Class</u> | |||
* 1% film prepared in Erlenmeyer flask looked the best, was uniform, etc. | |||
* 0.1% and 9% films were not uniform, had lumps of PVOH | |||
* The poor quality of the films was attributed to the high molecular weight of the PVOH. | |||
Revision as of 16:17, 11 February 2013
Experimental Chemistry | <html><img src="/images/9/94/Report.png" border="0" /></html> Main project page <html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>Previous entry<html> </html>Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html> |
ObjectiveTo crosslink the films prepared last class, to test the effects of using a lower molecular weight PVOH on the film, and to prepare a 0.2 M NaOH solution for use next class. DescriptionCrosslinking
Preparation of Lower Weight PVOH Films
(0.5 moles/L)(X) = (0.2 moles/L)(0.05 L) → X = 0.02 L = 20 mL
DataNo data was collected today. NotesDescription of Films Prepared Last Class
|