User:Elizabeth Ghias/Notebook/Experimental Chemistry/2012/09/07: Difference between revisions
No edit summary |
No edit summary |
||
(8 intermediate revisions by the same user not shown) | |||
Line 11: | Line 11: | ||
==Objective== | ==Objective== | ||
To conduct Differential Scanning Calorimetry | To conduct Differential Scanning Calorimetry, to complete the cross-linking reactions conducted last week, and to finish evaporating water from the two films made on Wednesday. | ||
Line 19: | Line 19: | ||
# The masses of three DSC pans and lids were measured. | # The masses of three DSC pans and lids were measured. | ||
# 3 ± 0.3 mg of film (Films 1, 3, and 5 were used) were added to each pan. | # 3 ± 0.3 mg of film (Films 1, 3, and 5 were used, see below) were added to each pan. | ||
# Each pan and lid were placed into the press. | # Each pan and lid were placed into the press. | ||
# The three samples were placed into the DSC in spaces 6,7, and 8. | # The three samples were placed into the DSC in spaces 6,7, and 8. | ||
# The DSC was run for the three trials with the following program: | # The DSC was run for the each of the three trials with the following program: | ||
## Equilibrate (20.00°C) | ## Equilibrate (20.00°C) | ||
## Ramp (20°C/min to 240°C/min) | ## Ramp (20°C/min to 240°C/min) | ||
Line 30: | Line 30: | ||
<u>Crosslinking Reactions</u> | |||
0.2 g of Films 2,4,5,6, and 7 (See below for list of films) were placed into an oven set to 90°C for 90 minutes. | |||
<u>Evaporation of Films made on 9/5</u> | |||
* The films made on Wednesday were placed on a hot plate to allow excess water left in the films to evaporate. | |||
** One film contained 0.5014 g PVA (MW = 22,000) in 5 mL water, with 0.0554 g succinic acid and 3 drops of phosphoric acid | |||
** The other film consisted of 0.5067 g PVA (MW = 22,000) in 5 mL water, with 0.0562 g maleic acid and 3 drops of phosphoric acid | |||
<u>List of Films</u> | |||
* Film 1 = 0.5110 g PVA (MW = 22,000) in 3 mL H<sub>2</sub>O, no acid | |||
* Film 2 = 1.0084 g PVA (MW = 22,000) in 6 mL H<sub>2</sub>O, no acid | |||
* Film 3 = 0.5078 g PVA (MW = 22,000) in 3 mL H<sub>2</sub>O, with 3 drops of HCl | |||
* Film 4 = 1.0044 g PVA (MW = 22,000) in 6 mL H<sub>2</sub>O, with 3 drops of HCl | |||
* Film 5 = 0.5066 g PVA (MW = 22,000) in 3 mL H<sub>2</sub>O, with 0.05 g succinic acid and 3 drops of HCl | |||
* Film 6 = 0.50 g PVA (MW = 22,000) in 3 mL H<sub>2</sub>O, with 0.05 g Maleic acid and 3 drops of HCl | |||
* Film 7 = 1.0010 g PVA (MW = 22,000) in 6 mL H<sub>2</sub>O, with 3 drops of phosphoric acid | |||
* Film 8 = 0.5053 g PVA (MW = 22,000) in 3 mL H<sub>2</sub>O, with 3 drops of phosphoric acid | |||
==Data== | ==Data== | ||
* | |||
<u>Differential Scanning Calorimetry</u> | |||
Trial 1 (Film 1) - mass of pan and lid = 0.05002 g, mass of pan and lid with material = 0.05285 g | |||
Trial 2 (Film 3) - mass of pan and lid = 0.04993 g, mass of pan and lid with material = 0.05317 g | |||
Trial 3 (Film 5) - mass of pan and lid = 0.04880 g, mass of pan and lid with material = 0.05132 g | |||
<u>Crosslinking Reactions</u> | |||
After 90 minutes in the oven: | |||
* Film 2 - color remained the same, film became harder/more brittle | |||
* Film 4 - color changed from clear to black/red depending on the thickness of the film. Thicker portions of the film were darker than thinner parts, which appeared red. The black parts of the film were very hard, while the thinner parts of the film were more flexible. | |||
* Film 5 - color changed from clear to black, film became harder/more brittle | |||
* Film 6 - color changed from clear to black, film became harder/more brittle | |||
* Film 7 - Film remained the same | |||
==Notes== | ==Notes== | ||
* The color change from clear to black is the result of the crosslinking that occurred in the presence of the acid. | |||
* Film 7 remained the same because a weak acid was added, not a strong acid. | |||
* The hot plate used to evaporate the excess water from the films made on Wednesday was too hot and thus, bubbling was observed in the films. We will remake the films on Monday. | |||
Revision as of 20:03, 25 November 2012
Experimental Chemistry | <html><img src="/images/9/94/Report.png" border="0" /></html> Main project page <html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>Previous entry<html> </html>Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html> |
ObjectiveTo conduct Differential Scanning Calorimetry, to complete the cross-linking reactions conducted last week, and to finish evaporating water from the two films made on Wednesday.
DescriptionDifferential Scanning Calorimetry
0.2 g of Films 2,4,5,6, and 7 (See below for list of films) were placed into an oven set to 90°C for 90 minutes.
DataDifferential Scanning Calorimetry Trial 1 (Film 1) - mass of pan and lid = 0.05002 g, mass of pan and lid with material = 0.05285 g Trial 2 (Film 3) - mass of pan and lid = 0.04993 g, mass of pan and lid with material = 0.05317 g Trial 3 (Film 5) - mass of pan and lid = 0.04880 g, mass of pan and lid with material = 0.05132 g
After 90 minutes in the oven:
Notes
|