User:Allison K. Alix/Notebook/CHEM-581/2012/10/03: Difference between revisions
(fix raw html notebook nav) |
|||
(12 intermediate revisions by one other user not shown) | |||
Line 2: | Line 2: | ||
|- | |- | ||
|style="background-color: #EEE"|[[Image:BDLlogo_notext_lr.png|128px]]<span style="font-size:22px;"> Experimental Chemistry</span> | |style="background-color: #EEE"|[[Image:BDLlogo_notext_lr.png|128px]]<span style="font-size:22px;"> Experimental Chemistry</span> | ||
|style="background-color: #F2F2F2" align="center"| | |style="background-color: #F2F2F2" align="center"|[[File:Report.png|frameless|link={{#sub:{{FULLPAGENAME}}|0|-11}}]][[{{#sub:{{FULLPAGENAME}}|0|-11}}|Main project page]]<br />{{#if:{{#lnpreventry:{{FULLPAGENAME}}}}|[[File:Resultset_previous.png|frameless|link={{#lnpreventry:{{FULLPAGENAME}}}}]][[{{#lnpreventry:{{FULLPAGENAME}}}}{{!}}Previous entry]] }}{{#if:{{#lnnextentry:{{FULLPAGENAME}}}}|[[{{#lnnextentry:{{FULLPAGENAME}}}}{{!}}Next entry]][[File:Resultset_next.png|frameless|link={{#lnnextentry:{{FULLPAGENAME}}}}]]}} | ||
|- | |- | ||
| colspan="2"| | | colspan="2"| | ||
Line 13: | Line 13: | ||
==Description== | ==Description== | ||
Dimensional Mechanical Analysis will be performed on previously synthesized PVOH films consisting of the following: 1) MW: 22000 2) MW: 100000 3) MW: 22000 with phosphoric acid 4) MW: 100000 with hydrochloric acid 5) MW: 22000 with phosphoric acid and maleic acid. Samples 3-5 were crosslinked via dehydration in the oven at | Dimensional Mechanical Analysis (DMA) will be performed on previously synthesized PVOH films consisting of the following: | ||
1) MW: 22000 | |||
2) MW: 100000 | |||
3) MW: 22000 with phosphoric acid | |||
4) MW: 100000 with hydrochloric acid | |||
5) MW: 22000 with phosphoric acid and maleic acid. | |||
Samples 3-5 were crosslinked via dehydration in the oven at 120°C for 90 minutes. Samples of films 1 and 2 were also cross linked via dehydration for a before and after comparison of crosslinking. | |||
==Data== | ==Data== | ||
<u>PVOH MW: 22000</u> | |||
height: 20.49mm | |||
width: 0.22mm. | |||
The films that were cross-linked in the oven had some considerable changes in color and toughness: | |||
*MW 100,000: film became much tougher, no visible color changes. | |||
*MW 22000: no toughness or color changes. | |||
*MW 22000 w/ phosphoric acid: film became much tougher and turned a slight yellowish brown color. | |||
*MW 22000 with phosphoric acid and maleic acid: no changes in toughness or color. | |||
*MW: 100,000 w/ hydrochloric acid: toughness did not change but color became a very dark black | |||
==Notes== | |||
A non-cross linked sample of film 1 will have to be re-analyzed as the length was entered as 3.5mm instead of 5.3mm | |||
Latest revision as of 22:05, 26 September 2017
Experimental Chemistry | Main project page Previous entry Next entry |
ObjectiveDynamic Mechanical Analysis of PVOH films DescriptionDimensional Mechanical Analysis (DMA) will be performed on previously synthesized PVOH films consisting of the following: 1) MW: 22000 2) MW: 100000 3) MW: 22000 with phosphoric acid 4) MW: 100000 with hydrochloric acid 5) MW: 22000 with phosphoric acid and maleic acid. Samples 3-5 were crosslinked via dehydration in the oven at 120°C for 90 minutes. Samples of films 1 and 2 were also cross linked via dehydration for a before and after comparison of crosslinking. DataPVOH MW: 22000 height: 20.49mm width: 0.22mm. The films that were cross-linked in the oven had some considerable changes in color and toughness:
NotesA non-cross linked sample of film 1 will have to be re-analyzed as the length was entered as 3.5mm instead of 5.3mm
|