User:Allison K. Alix/Notebook/CHEM-581/2012/10/03

From OpenWetWare

< User:Allison K. Alix | Notebook | CHEM-581 | 2012 | 10(Difference between revisions)
Jump to: navigation, search
(Data)
Current revision (13:52, 5 October 2012) (view source)
(Data)
 
(3 intermediate revisions not shown.)
Line 13: Line 13:
==Description==
==Description==
-
Dimensional Mechanical Analysis will be performed on previously synthesized PVOH films consisting of the following: 1) MW: 22000 2) MW: 100000 3) MW: 22000 with phosphoric acid 4) MW: 100000 with hydrochloric acid 5) MW: 22000 with phosphoric acid and maleic acid. Samples 3-5 were crosslinked via dehydration in the oven at 120 degrees celsius for 90 minutes. Samples of films 1 and 2 were also cross linked via dehydration for a before and after comparison of crosslinking.
+
Dimensional Mechanical Analysis (DMA) will be performed on previously synthesized PVOH films consisting of the following:  
 +
 
 +
1) MW: 22000  
 +
 
 +
2) MW: 100000  
 +
 
 +
3) MW: 22000 with phosphoric acid  
 +
 
 +
4) MW: 100000 with hydrochloric acid  
 +
 
 +
5) MW: 22000 with phosphoric acid and maleic acid.  
 +
 
 +
Samples 3-5 were crosslinked via dehydration in the oven at 120°C for 90 minutes. Samples of films 1 and 2 were also cross linked via dehydration for a before and after comparison of crosslinking.
==Data==
==Data==
-
'''PVOH MW: 22000''' height: 20.49mm width: 0.22mm. The films that were cross-linked in the oven had some considerable changes in color and toughness. MW 100,000: film became much tougher, no visible color changes. MW 22000: no toughness or color changes. MW 22000 w/ phosphoric acid: film became much tougher and turned a slight yellowish brown color. MW 22000 with phosphoric acid and maleic acid: no changes in toughness or color. MW: 100,000 w/ hydrochloric acid: toughness did not change but color became a very dark black
+
<u>PVOH MW: 22000</u>
 +
 
 +
height: 20.49mm  
 +
 
 +
width: 0.22mm.  
 +
 
 +
The films that were cross-linked in the oven had some considerable changes in color and toughness:
 +
 
 +
*MW 100,000: film became much tougher, no visible color changes.  
 +
*MW 22000: no toughness or color changes.  
 +
*MW 22000 w/ phosphoric acid: film became much tougher and turned a slight yellowish brown color.  
 +
*MW 22000 with phosphoric acid and maleic acid: no changes in toughness or color.  
 +
*MW: 100,000 w/ hydrochloric acid: toughness did not change but color became a very dark black
==Notes==
==Notes==

Current revision

Experimental Chemistry Main project page
Previous entry      Next entry


Objective

Dynamic Mechanical Analysis of PVOH films

Description

Dimensional Mechanical Analysis (DMA) will be performed on previously synthesized PVOH films consisting of the following:

1) MW: 22000

2) MW: 100000

3) MW: 22000 with phosphoric acid

4) MW: 100000 with hydrochloric acid

5) MW: 22000 with phosphoric acid and maleic acid.

Samples 3-5 were crosslinked via dehydration in the oven at 120°C for 90 minutes. Samples of films 1 and 2 were also cross linked via dehydration for a before and after comparison of crosslinking.

Data

PVOH MW: 22000

height: 20.49mm

width: 0.22mm.

The films that were cross-linked in the oven had some considerable changes in color and toughness:

  • MW 100,000: film became much tougher, no visible color changes.
  • MW 22000: no toughness or color changes.
  • MW 22000 w/ phosphoric acid: film became much tougher and turned a slight yellowish brown color.
  • MW 22000 with phosphoric acid and maleic acid: no changes in toughness or color.
  • MW: 100,000 w/ hydrochloric acid: toughness did not change but color became a very dark black

Notes

A non-cross linked sample of film 1 will have to be re-analyzed as the length was entered as 3.5mm instead of 5.3mm