User:Allison K. Alix/Notebook/CHEM-581/2012/10/03: Difference between revisions
(→Data) |
(→Data) |
||
(4 intermediate revisions by the same user not shown) | |||
Line 13: | Line 13: | ||
==Description== | ==Description== | ||
Dimensional Mechanical Analysis will be performed on previously synthesized PVOH films consisting of the following: 1) MW: 22000 2) MW: 100000 3) MW: 22000 with phosphoric acid 4) MW: 100000 with hydrochloric acid 5) MW: 22000 with phosphoric acid and maleic acid. Samples 3-5 were crosslinked via dehydration in the oven at | Dimensional Mechanical Analysis (DMA) will be performed on previously synthesized PVOH films consisting of the following: | ||
1) MW: 22000 | |||
2) MW: 100000 | |||
3) MW: 22000 with phosphoric acid | |||
4) MW: 100000 with hydrochloric acid | |||
5) MW: 22000 with phosphoric acid and maleic acid. | |||
Samples 3-5 were crosslinked via dehydration in the oven at 120°C for 90 minutes. Samples of films 1 and 2 were also cross linked via dehydration for a before and after comparison of crosslinking. | |||
==Data== | ==Data== | ||
<u>PVOH MW: 22000</u> | |||
height: 20.49mm | |||
width: 0.22mm. | |||
The films that were cross-linked in the oven had some considerable changes in color and toughness: | |||
*MW 100,000: film became much tougher, no visible color changes. | |||
*MW 22000: no toughness or color changes. | |||
*MW 22000 w/ phosphoric acid: film became much tougher and turned a slight yellowish brown color. | |||
*MW 22000 with phosphoric acid and maleic acid: no changes in toughness or color. | |||
*MW: 100,000 w/ hydrochloric acid: toughness did not change but color became a very dark black | |||
==Notes== | ==Notes== |
Revision as of 10:52, 5 October 2012
Experimental Chemistry | <html><img src="/images/9/94/Report.png" border="0" /></html> Main project page <html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>Previous entry<html> </html>Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html> |
ObjectiveDynamic Mechanical Analysis of PVOH films DescriptionDimensional Mechanical Analysis (DMA) will be performed on previously synthesized PVOH films consisting of the following: 1) MW: 22000 2) MW: 100000 3) MW: 22000 with phosphoric acid 4) MW: 100000 with hydrochloric acid 5) MW: 22000 with phosphoric acid and maleic acid. Samples 3-5 were crosslinked via dehydration in the oven at 120°C for 90 minutes. Samples of films 1 and 2 were also cross linked via dehydration for a before and after comparison of crosslinking. DataPVOH MW: 22000 height: 20.49mm width: 0.22mm. The films that were cross-linked in the oven had some considerable changes in color and toughness:
NotesA non-cross linked sample of film 1 will have to be re-analyzed as the length was entered as 3.5mm instead of 5.3mm
|