===New film synthesis===
* 1.0084 g of 22,000 MW PVA and 0.1105 g of NaMT were hydrated with 7 mL of distilled water
* 1.0020 g of 22,000 MW PVA were hydrated with 7 mL distilled water
* Heated at approx. 80ºC under gentle stirring until all crystals were dissolved
* Cooled to room temperature
* Added 0.5 mL 0.8% wt glutaraldehyde
* Stirred for 3 min to ensure homogeneity
* Poured into teflon dish


===Completion of ionic modified clays===
*Completed synthesis from [http://openwetware.org/wiki/User:Alicia_Rasines_Mazo/Notebook/CHEM-581_Experimental_Chemistry_I/2014/10/03 Oct. 3]




Revision as of 09:59, 17 October 2014

Project name <html><img src="/images/9/94/Report.png" border="0" /></html> Main project page
<html><img src="/images/c/c3/Resultset_previous.png" border="0" /></html>Previous entry<html>&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;&nbsp;</html>Next entry<html><img src="/images/5/5c/Resultset_next.png" border="0" /></html>

Tasks for October 17

  • To begin synthesis of PVa and 10% wt PVA-Clay films
  • To complete synthesis of cation exchange modified clays
  • To determine density of films
  • To complete data analysis

New film synthesis

  • 1.0084 g of 22,000 MW PVA and 0.1105 g of NaMT were hydrated with 7 mL of distilled water
  • 1.0020 g of 22,000 MW PVA were hydrated with 7 mL distilled water
  • Heated at approx. 80ºC under gentle stirring until all crystals were dissolved
  • Cooled to room temperature
  • Added 0.5 mL 0.8% wt glutaraldehyde
  • Stirred for 3 min to ensure homogeneity
  • Poured into teflon dish

Completion of ionic modified clays

  • Completed synthesis from Oct. 3